Effect of elaboration velocity on magnetic properties of melt spun amorphous metal ribbons
نویسندگان
چکیده
2014 Fe74.7Cr3.8P8.7C10.7Si1.9 amorphous alloy in ribbon shape have been obtained by melt spinning with substrate velocity in the range 20-46 ms-1. Magnetic properties of as-quenched samples are studied by different techniques : the ribbon’s magnetic texture by Mössbauer spectroscopy, the magnetization, coercive field and Curie temperature by investigation of B-H loops at 50 Hz. The experimental results give evidence for correlation between ribbon width and magnetic texture only. Revue Phys. Appl. 22 (1987) 729-734 AOÛT 1987, Classification Physics Abstracts 75.50K 76.80
منابع مشابه
Effect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons
In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...
متن کاملساختار و خواص مغناطیسی آلیاژهای CoFeSiB انجماد سریع یافته
The effects of metalloids Si(4-27 at%) and B(5-22 at%) on the structure and magnetic properties of melt spun cobalt based alloys containing 5at% Fe have been studied. XRD results revealed that in non-eutectic ternary CoFeSi and CoFeB alloys, the additions of Si or B, alone can not lead to full amorphization of melt spun ribbons. In quaternary CoFeSiB alloys, the total amounts of Si and B additi...
متن کاملIntroducing and investigating structural and magnetic properties of ribbons Co68.5-xFe4WxSi16.5B11 (x = 0.8, 2) in amorphous and crystalline states
In this study, for the first time, cobalt base ribbons were made by adding two different amounts of tungsten with Co67.7Fe4W0.8Si16.5B11 and Co66.5Fe4W2 Si16.5B11 compounds by melt spinning in the water. The pattern of X-ray diffraction taken from these ribbons shows that these magnetic ribbons are amorphous. By using thermal analysis curves, taken from the ribbons, crystallization temperature...
متن کاملDip coating of silica layer on melt-spun Finemet ribbons: surface morphology and electrical resistivity changes
In this study, melt-spun Finemet ribbons were coated by a thin layer of SiO2 using dip coating method. Amorphous ribbon prepared by melt spinning method and dip coating were done by using a solution of tetraethylen orthosilicate as a SiO2 precursor, ethanol as solvent and distilled water for hydrolysis. Different thicknesses of SiO2 layer, namely 304, 349, 451, 526 and 970 nm were obtained prop...
متن کاملNanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کامل