Growth characteristics of primary M7C3 carbide in hypereutectic Fe-Cr-C alloy

نویسندگان

  • Sha Liu
  • Yefei Zhou
  • Xiaolei Xing
  • Jibo Wang
  • Xuejun Ren
  • Qingxiang Yang
چکیده

The microstructure of the hypereutectic Fe-Cr-C alloy is observed by optical microscopy (OM). The initial growth morphology, the crystallographic structure, the semi-molten morphology and the stacking faults of the primary M7C3 carbide are observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The in-suit growth process of the primary M7C3 carbide was observed by confocal laser microscope (CLM). It is found that the primary M7C3 carbide in hypereutectic Fe-Cr-C alloy is irregular polygonal shape with several hollows in the center and gaps on the edge. Some primary M7C3 carbides are formed by layers of shell or/and consist of multiple parts. In the initial growth period, the primary M7C3 carbide forms protrusion parallel to {} crystal planes. The extending and revolving protrusion forms the carbide shell. The electron backscattered diffraction (EBSD) maps show that the primary M7C3 carbide consists of multiple parts. The semi-molten M7C3 carbide contains unmelted shell and several small-scale carbides inside, which further proves that the primary M7C3 carbide is not an overall block. It is believed that the coalescence of the primary M7C3 carbides is ascribed to the growing condition of the protrusion and the gap filling process.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Chromium Content on Microstructure and Wear Resistance of Fe-Cr-C Hard facing Layers

Layers of Fe-Cr-C Hard facing material containing various amounts of chromium were deposited on mild steel base metal. Optical Microscope (OM), Scanning Electron Microscope (SCM) and X-ray diffraction (XRD) were used to investigate the effect of chromium content of micro structural characteristics of Fe-Cr-C hard facing layers. The M7C3 carbide refinement mechanism exists on base metal. The exp...

متن کامل

SLURRY EROSION RESISTANCE OF LASER CLAD Fe–Cr–B–Si COATINGS

The slurry erosion behaviour of laser clad Fe–Cr–B–Si alloy coatings was investigated at impact angles from 30u to 90u with an increment of 15u, and compared with the slurry erosion behaviour of two laser clad carbide coatings and a non-coated substrate made of AISI 4140 steel. The Fe–Cr–B–Si alloy coatings had slurry erosion resistance. Their overall slurry erosion resistance at impact angles ...

متن کامل

Study on Microstructure and Mechanical Properties of Hypereutectic Al–18Si Alloy Modified with Al–3B

An hypereutectic Al-18Si alloy was modified via an Al-3B master alloy. The effect of the added Al-3B and the modification temperature on the microstructure, tensile fracture morphologies, and mechanical properties of the alloy were investigated using an optical microscope, Image-Pro Plus 6.0, a scanning electron microscope, and a universal testing machine. The results show that the size of the ...

متن کامل

Effect of Al–5Ti–C Master Alloy on the Microstructure and Mechanical Properties of Hypereutectic Al–20%Si Alloy

Al-5Ti-C master alloy was prepared and used to modify hypereutectic Al-20%Si alloy. The microstructure evolution and mechanical properties of hypereutectic Al-20%Si alloy with Al-5Ti-C master alloy additions (0, 0.4, 0.6, 1.0, 1.6 and 2.0 wt%) were investigated. The results show that, Al-5Ti-C master alloy (0.6 wt%, 10 min) can significantly refine both eutectic and primary Si of hypereutectic ...

متن کامل

Stability of eutectic carbide in Fe-Cr-Mo-W-V-C alloy

The stability of the eutectic carbide in a self-designed Fe-Cr-Mo-W-V-C alloy during solidifi atio as a alyzed i this ork. The ar ide pre ipitatio rule of the steel was calculated by Thermo-Calc.The typical microstructures at 1240 °C and 1200 °C ere o ser ed y opti al i ros ope OM ,field e issio s a i g ele tro microscope (FESEM) and transmission electron microscope (TEM). The selected area dif...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2016