Cellulose nanofibrils as filler for adhesives: effect on specific fracture energy of solid wood-adhesive bonds

نویسندگان

  • Stefan Veigel
  • Ulrich Müller
  • Jozef Keckes
  • Michael Obersriebnig
  • Wolfgang Gindl-Altmutter
چکیده

Cellulose nanofibrils were prepared by mechanical fibrillation of never-dried beech pulp and bacterial cellulose. To facilitate the separation of individual fibrils, one part of the wood pulp was surface-carboxylated by a catalytic oxidation using (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO) as a catalyst. After fibrillation by a high pressure homogenizer, the obtained aqueous fibril dispersions were directly mixed with different urea-formaldehyde-(UF)-adhesives. To investigate the effect of added cellulose filler on the fracture mechanical properties of wood adhesive bonds, double cantilever beam specimens were prepared from spruce wood. While the highest fracture energy values were observed for UF-bonds filled with untreated nanofibrils prepared from wood pulp, bonds filled with TEMPO-oxidized fibrils showed less satisfying performance. It is proposed that UF-adhesive bonds can be significantly toughened by the addition of only small amounts of cellulose nanofibrils. Thereby, the optimum filler content is largely depending on the adhesive and type of cellulose filler used.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Cellulose fibers and nanofibrils for adhesive reinforcement

Introduction In wood industry, adhesive bonding is one of the key process steps. To ensure continuing technological progress in wood industry it is necessary to explore new possibilities of improvement in adhesive bonding. The potential routes for performance improvements suggested by a state of the art report issued by COST Action E13 Wood Adhesion and Glued Products (Dunky et al. 2002) focus ...

متن کامل

Adhesives for Achieving Durable Bonds with Acetylated Wood

Acetylation of wood imparts moisture durability, decay resistance, and dimensional stability to wood; however, making durable adhesive bonds with acetylated wood can be more difficult than with unmodified wood. The usual explanation is that the acetylated surface has fewer hydroxyl groups, resulting in a harder-to-wet surface and in fewer hydrogen bonds between wood and adhesive. This concept w...

متن کامل

Adhesion Mechanisms of Durable Wood Adhesive Bonds

This chapter presents and discusses the current state of the art regarding adhesion mechanisms in characterizing durable adhesive bonds for wood composites. Particular emphasis is placed on phenol-formaldehyde (PF) and polymeric methylene diphenyl diisocyanate (pMDI) adhesives. An overview of current adhesion mechanisms is presented with an emphasis on categorizing adhesion mechanisms relative ...

متن کامل

Nanopaper Properties and Adhesive Performance of Microfibrillated Cellulose from Different (Ligno-)Cellulosic Raw Materials

The self-adhesive potential of nanocellulose from aqueous cellulosic suspensions is of interest with regard to a potential replacement of synthetic adhesives. In order to evaluate the performance of microfibrillated cellulose from different (ligno-)cellulosic raw materials for this purpose, softwood and hardwood powder were fibrillated and compared to sugar beet pulp as a representative non-woo...

متن کامل

Mode-I Fracture in Bonded Wood: Studies of Adhesive Thermal Stability, and of the Effects of Wood Surface Deactivation

This work included two separate studies; the common theme in each was the use of mode-I fracture testing to evaluate wood adhesion. In the first study, mode-I fracture testing was used to compare the thermal stability of polyurethane (PUR) and resorcinol-formaldehyde (RF) wood adhesives. Bonded specimens for both adhesives were subjected to prolonged thermal exposure, and fracture testing was s...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 18  شماره 

صفحات  -

تاریخ انتشار 2011