Ceramic Head Fracture in Ceramic-on-Polyethylene Total Hip Arthroplasty
نویسندگان
چکیده
Revision rates of total hip arthroplasty have decreased after introducing total hip arthroplasty (THA) using ceramic component, since ceramic components could reduce components wear and osteolysis. The fracture of a ceramic component is a rare but potentially serious event. Thus, ceramic on polyethylene articulation is gradually spotlighted to reduce ceramic component fracture. There are a few recent reports of ceramic head fracture with polyethylene liner. Herein, we describe a case of a ceramic head component fracture with polyethylene liner. The fractured ceramic head was 28 mm short neck with conventional polyethylene liner. We treated the patient by total revision arthroplasty using 4th generation ceramic on ceramic components.
منابع مشابه
Fatal Cobalt Cardiomyopathy Following Revision Total Hip Arthroplasty – A Brief Report with Review of Literature
Ceramic bearing surfaces are being increasingly used in young patients undergoing total hip arthroplasty. However,failures have been reported including fractures even with the newer third generation ceramics. The recommendedtreatment for fracture of ceramic bearing surfaces is complete synovectomy and revision total hip arthroplasty.However, disappointing results have also bee...
متن کاملSevere metallosis leading to femoral head perforation.
This article describes a case of severe metallosis in a 67-year-old woman who initially underwent primary total hip arthroplasty with a ceramic-on-ceramic articular bearing. This was subsequently revised to a metal-on-polyethylene articulation due to ceramic liner fracture. She presented with severe hip pain and a pelvic mass. Infective workup was negative. Perforation of the cobalt-chrome femo...
متن کاملMetallosis after Exchange of the Femoral Head and Liner following Ceramic Acetabular Liner Dissociation in Total Hip Arthroplasty with a Modular Layered Acetabular Component
The type of bearing material that should be used in revision surgery after the failure of ceramic-on-ceramic total hip arthroplasty (THA) remains controversial. In the case of ceramic fracture, the residual ceramic particles can cause consequent metallosis when metal implants are used for revision THA. On the other hand, in the case of THA failure without ceramic fracture, revision THA with a m...
متن کاملA late dissociation of the ceramic component of a sandwich liner cup in a total hip arthroplasty—Case report and review of the literature
We present a case of a 71-year-old woman with unexplained instability of her total hip arthroplasty 12 years after implantation due to loosening of the ceramic component of a sandwich ceramic in polyethylene liner. She experienced in total 2 dislocations in 6 months. These events occurred without fracture of the ceramic liner. Sandwich ceramic liners were introduced with the idea of combining t...
متن کاملRepeated Ceramic Head Fracture after Ceramic-on-ceramic Total Hip Arthroplasty
Early generation ceramic articulations were problematic in terms of ceramic implant fracture and wear. Although the mechanical properties of ceramic material have improved during the last three decades, ceramic component fracture remains an issue. Many authors have reported fractures of the ceramic head, and a few have described ceramic acetabular insert fracture. However, these complications a...
متن کامل