Shape and size control of Ag2Se nanocrystals from a single precursor [(Ph3P)3Ag2(SeC{O}Ph)2].
نویسندگان
چکیده
Monodispersed Ag2Se nanocubes and faceted nanocrystals have been synthesized by hexadecylamine (HDA) induced thermolysis of [(PPh3)3Ag2(SeC{O}Ph)2] in a mixture of TOP (tri-n-octyl phosphine) and HDA in the temperature range 95-180 degrees C.
منابع مشابه
One-pot synthesis and third-order nonlinear optical properties of AgInS2 nanocrystals.
Good quality colloidal nanocrystals of metastable orthorhombic phase of AgInS2 obtained by decomposing the single-precursor [(Ph3P)2AgIn(SCOPh)4] in a mixture of dodecanethiol and oleic acid at 125-200 degrees C, exhibit significant third order non-linear optical properties.
متن کاملFabrication and Characterization of Nanoporous Co Oxide (Co3O4) Prepared by Simple Sol-gel Synthesis
Cobalt oxide (Co3O4) nanorods were prepared by a simple co-precipitation method using ethanol solution of cobalt nitrate as precursor and cetyl trimethylammonium bromide (CTAB) as surfactant. Morphological properties of the nanoparticles were characterized. XRD measurement exhibited the structure of Co3O4 nanocrystals for annealed samples. The SEM ima...
متن کاملFabrication and Characterization of Rutile TiO2 Nanocrystals by Water Soluble Precursor
In this research, TiO2 nanoparticles were synthesized by a simple wet chemical method. TiCl4 was used as precursor in hydrogen peroxideand ethanol. The TiO2 nanoparticles were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron dispersive spectroscopy (EDS) and UV-Vis spectrophotome...
متن کاملSub-10 nm platinum nanocrystals with size and shape control: catalytic study for ethylene and pyrrole hydrogenation.
Platinum nanocubes and nanopolyhedra with tunable size from 5 to 9 nm were synthesized by controlling the reducing rate of metal precursor ions in a one-pot polyol synthesis. A two-stage process is proposed for the simultaneous control of size and shape. In the first stage, the oxidation state of the metal ion precursors determined the nucleation rate and consequently the number of nuclei. The ...
متن کاملCRYSTALLOGRAPHIC, MORPHOLOGICAL AND W-H MODELS INVESTIGATIONS ON Mn SUBSTITUTED ZnO NANOCRYSTALS
Mn doped ZnO nanocrystals were prepared by co-precipitation route sintered at 450 °C temperature. XRD results indicate that the samples having hexagonal (wurtzite) structure. From X-ray data it is found that the lattice parameters increase with increasing Mn concentration. The X-ray density decreases with increasing Mn concentration of Zn 1-x Mnx O nanocrystals. It indicates that the Mn...