Sulfur and Water Resistance of Mn-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOx: A Review
نویسندگان
چکیده
Selective catalytic reduction (SCR) with NH3 is the most efficient and economic flue gas denitrification technology developed to date. Due to its high low-temperature catalytic activity, Mn-based catalysts present a great prospect for application in SCR de-NOx at low temperatures. However, overcoming the poor resistance of Mn-based catalysts to H2O and SO2 poison is still a challenge. This paper reviews the recent progress on the H2O and SO2 resistance of Mn-based catalysts for the low-temperature SCR of NOx. Firstly, the poison mechanisms of H2O and SO2 are introduced in detail, respectively. Secondly, Mn-based catalysts are divided into three categories—single MnOx catalysts, Mn-based multi-metal oxide catalysts, and Mn-based supported catalysts—to review the research progress of Mn-based catalysts for H2O and SO2 resistance. Thirdly, several strategies to reduce the poisonous effects of H2O and SO2, such as metal modification, proper support, the combination of metal modification and support, the rational design of structure and morphology, are summarized. Finally, perspectives and future directions of Mn-based catalysts for the low-temperature SCR of NOx are proposed.
منابع مشابه
Low temperature selective catalytic reduction of NOx with NH3 over Mn-based catalyst: A review
The removals of NOx by catalytic technology at low temperatures (100–300 °C) for industrial flue gas treatment have received increasing attention. However, the development of low temperature catalysts for selective catalytic reduction (SCR) of NOx with ammonia is still a challenge especially in the presence of SO2. The current status of using Mn-based catalysts for low temperature SCR of NOx wi...
متن کاملIron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3.
The catalysts of iron-doped Mn-Ce/TiO2 (Fe-Mn-Ce/TiO2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction (SCR) of NO with NH3. It was found that the NO conversion over Fe-Mn-Ce/TiO2 was obviously improved after iron doping compared with that over Mn-Ce/TiO2. Fe-Mn-Ce/TiO2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity. The results...
متن کاملOptimization and Modeling of CuOx/OMWNT’s for Catalytic Reduction of Nitrogen Oxides by Response Surface Methodology
A series of copper oxide (CuOx) catalysts supported by oxidized multi-walled carbon nanotubes (OMWNT’s) were prepared by the wet impregnation method for the low temperature (200 °C) selective catalytic reduction of nitrogen oxides (NOx) using NH3 as a reductant agent in the presence of excess oxygen. These catalysts were characterized by FTIR, XRD, SEM-EDS, and H2-TPR meth...
متن کاملPoisoning Effect of SO2 on Honeycomb Cordierite- Based Mn–Ce/Al2O3Catalysts for NO Reduction with NH3 at Low Temperature
Honeycomb cordierite-based Mn–Ce/Al2O3 catalysts were prepared by the impregnation method and used for low-temperature selective catalytic reduction (SCR) of NOx with NH3, with and without SO2 and/or H2O in a homemade fixed-bed tubular reactor. The catalyst reached nearly 80% NOx conversion at 100 ◦C in the absence of SO2. However, SO2 reduces the catalytic activity (80% to 72%) of the honeycom...
متن کاملBauxite-supported Transition Metal Oxides: Promising Low-temperature and SO2-tolerant Catalysts for Selective Catalytic Reduction of NOx
In order to develop low-temperature (below 200 °C) and SO2-tolerant catalysts for selective catalytic reduction (SCR) of NOx, a series of cheap M/bauxite (M = Mn, Ni and Cu) catalysts were prepared using bauxite as a support. Their SCR performances are much superior to typical V2O5/TiO2, the addition of M into bauxite results in significant promotion of NOx removal efficiency, especially at low...
متن کامل