F. Bridges, C. H. Booth, M. Anderson, G. H. Kwei, J. J. Neumeier, J. Snyder, J. Mitchell, J. S. Gardner, and E. Brosha Physics Department, University of California, Santa Cruz, California 95064 Los Alamos National Laboratory, Los Alamos, New Mexico 87545 Physics Department, Florida Atlantic University, Boca Raton, Florida 33431 JPL, California Institute of Technology, Pasadena, California 91109-8099 Argonne National Laboratory, Argonne, Illinois 60439 ~Received 1 February 2000; revised manuscript received 23 August 2000; published 1 May 2001!
منابع مشابه
Evidence of Magnetization-dependent Polaron Formation in Typeset Using Revt E X
X-ray-absorption fine-structure measurements at the Mn K-edge as a function of temperature were performed on samples of La 1−x Ca x MnO 3 and La 0.67 Pb 0.33 MnO 3. All samples have a metal-insulator (MI) transition near the ferromagnetic transition, except the Ca 0.5 sample, which does not have a MI transition. Near T c for the MI samples, the Debye-Waller σ 2 for the Mn-O atom-pair increases ...
متن کامل0 O ct 1 99 8 Hall Effect of La 2 / 3 ( Ca , Pb ) 1 / 3 MnO 3 Single Crystals near the Critical Temperature
The Hall resistivity ρ xy of a La 2/3 (Ca,Pb) 1/3 MnO 3 single crystal has been measured as a function of temperature and field. The overall behavior is similar to that observed previously in thin-films. At 5 K, ρ xy is positive and linear in field, indicating that the anomalous contribution R S is negligible. However, the effective carrier density in a free electron model is n ef f = 2.4 holes...
متن کاملAnalysis of the Local Structure around Eu and Mn Ions in Alkaline-Earth Silicate Phosphors for White Light Illumination
M2SiO4-based phosphors (M: alkaline-earth metal) that emit red to blue light are expected to offer high color rendering to white light-emitting diodes (LEDs) in combination with blue or near-UV excitation sources. It is very important for the complete control of the emission color to understand the crystal field around the active elements (rareearth and transition metals). XAFS spectroscopy is ...
متن کاملX-ray absorption spectroscopy studies of Ba(1-x)Ca(x)TiO3.
We report x-ray absorption near edge spectroscopy (XANES) of Ca and O K-edges of Ba(1-x)Ca(x)TiO3 (x = 0, 0.01, 0.08, 1) and understand the spectral features related to the electronic structure of these perovskites. The XANES spectra of Ca K-edge possess a pre-edge peak similar to other 3d transition metals like Ti, Ni when present in perovskite structure and provides information about p-type o...
متن کامل