Effect of ball milling on the local magnetic flux distribution and microstructure of in situ Fe/MgB2 conductors
نویسنده
چکیده
The effects of the precursor milling energy on the superconducting and microstructural homogeneity of Fe-sheathed MgB2 monocore wires and tapes have been investigated. The conductors were produced by the powder-in-tube method using drawing and rolling deformation methods and in situ reaction. Combined magnetooptical, structural and magnetization measurements were performed on MgB2 superconducting tapes prepared from differently milled precursors revealing hidden mechanisms controlling their critical current density. Local degradation of the superconducting properties observed in some analysed conductors has been identified and correlated with microstructural observations. Preprint of Journal of Alloys and Compounds 717 (2017) 164-170 DOI: 10.1016/j.jallcom.2017.05.083
منابع مشابه
Sintering and Characterizations of WC-20wt.% (Fe,Co) Nano-Structured Powders Developed by Ball-Milling
The aim of the present work is to study the effects of the nanostructured WC-20 wt. % (Fe,Co) with different ratios of iron to cobalt on the microstructure and hardness of sintered samples. Furthermore, a sample with a cobalt binder under the same condition was produced for the comparison purposes. The nanocomposite development, after different milling times, has been monitored by means of X-ra...
متن کاملThe Effect of sintering temperature on microstructure and hardness of milled WC- 20 wt.% equiatomic (Fe,Co) cemented carbides
In this study, WC–20 wt.% equiatomic (Fe,Co) powder mixture was milled in a planetary ball mill. The effects of different milling time (15 min, 5h, 10h, and 25 h) and sintering temperatures on the microstructure and mechanical properties of this equi-Fe substituted cermet were investigated. The structural evolution and the crystallite size changes of the powders during milling were monitored by...
متن کاملپیشرفتهای اخیر در زمینه ساخت سیم و نوار ابررسانای MgB2
MgB2 wire and tape were prepared using the powder in tube and reaction in-situ technique. All samples were characterized using the XRD, SEM, TEM, as well as transport and magnetic measurements. High transport and magnetic critical current density values have been obtained for metal-clad wires and tapes. Different sheath materials have been examined, but Fe appears to be the best sheath for MgB...
متن کاملEffect of milling time on the crystallite size and microstructure of Al2O3/Mo Nano composite
In this paper, the production of Al2O3-Mo nano-composites via mechanical milling was investigated. Molybdenum and alumina powders with certain ratios were grounded in a planetary ball mill at different times. XRD technique was used to determine the crystallite size of the milled powders. The microstructure of milled powders was studied using optical and electron microscopes. The crystallite siz...
متن کاملMECHANO-THERMAL REDUCTION OF HEMATITE AND ANATASE MIXTURE BY TWO DIFFERENT FORMS OF CARBON AS REDUCTANT FOR IN-SITU PRODUCTION OF Fe-T iC - NANO CRYSTALLINE COMPOSITE
In this research, two different carbonaceous materials (Graphite:G and Petrocoke:P) were separately compared in terms of the carbothermic reduction of hematite and anatase in order to synthesize Fe-TiC nanocrystalline composite by mechanically activated sintering method. Powders were activated in a planetary high-energy ball mill under argon atmosphere for 0, 2, 5, ...
متن کامل