A mixed solution-processed gate dielectric for zinc-tin oxide thin-film transistor and its MIS capacitance

نویسندگان

  • Hunho Kim
  • Young-Jin Kwack
  • Eui-Jung Yun
  • Woon-Seop Choi
چکیده

Solution-processed gate dielectrics were fabricated with the combined ZrO2 and Al2O3 (ZAO) in the form of mixed and stacked types for oxide thin film transistors (TFTs). ZAO thin films prepared with double coatings for solid gate dielectrics were characterized by analytical tools. For the first time, the capacitance of the oxide semiconductor was extracted from the capacitance-voltage properties of the zinc-tin oxide (ZTO) TFTs with the combined ZAO dielectrics by using the proposed metal-insulator-semiconductor (MIS) structure model. The capacitance evolution of the semiconductor from the TFT model structure described well the threshold voltage shift observed in the ZTO TFT with the ZAO (1:2) gate dielectric. The electrical properties of the ZTO TFT with a ZAO (1:2) gate dielectric showed low voltage driving with a field effect mobility of 37.01 cm(2)/Vs, a threshold voltage of 2.00 V, an on-to-off current ratio of 1.46 × 10(5), and a subthreshold slope of 0.10 V/dec.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Zirconium oxide-aluminum oxide nanolaminate gate dielectrics for amorphous oxide semiconductor thin-film transistors

The dielectric properties of ZrO2–Al2O3 nanolaminates, deposited via atomic layer deposition, and their impact on the performance and stability of indium gallium zinc oxide and zinc tin oxide amorphous oxide semiconductor thin-film transistors TFTs are investigated. It is found that nanolaminate dielectrics can combine the advantages of constituent dielectrics and produce TFTs with improved per...

متن کامل

Fully solution-processed zinc oxide MIS capacitors by ultrasonic spray pyrolysis in air ambient

In this work, the fabrication and characterization of fully solution-processed zinc oxide metal–insulator–semiconductor (MIS) capacitors by ultrasonic spray pyrolysis (USP) are presented. Fluorine tin oxide by USP was used as transparent electrode, while spin-on glass by spin-coating was used as dielectric and zinc oxide by USP was used as active layer. Also, the zinc oxide film was characteriz...

متن کامل

Atomic layer deposited zinc tin oxide channel for amorphous oxide thin film transistors

Bottom-gate thin film transistors with amorphous zinc tin oxide channels were grown by atomic layer deposition. The films maintained their amorphous character up to temperatures over 500 C. The highest field effect mobility was 13 cm/V s with on-to-off ratios of drain current 10–10. The lowest subthreshold swing of 0.27 V/decade was observed with thermal oxide as a gate insulator. The channel l...

متن کامل

Reduced-temperature solution-processed transparent oxide low-voltage- operable field-effect transistors

Metal oxide-based transistors can be fabricated by low-cost, large-area solution processing methods, but involve a trade-off between low processing temperature, facile charge transport and high-capacitance/low-voltage transistor gates. We achieve these simultaneously by fabricating zinc oxide and sodium-incorporated alumina (SA) thin films with temperature not exceeding 200 to 250 °C using aque...

متن کامل

Bias-stress-stable solution-processed oxide thin film transistors.

We generated a novel amorphous oxide semiconductor thin film transistor (AOS-TFT) that has exellent bias-stress stability using solution-processed gallium tin zinc oxide (GSZO) layers as the channel. The cause of the resulting stable operation against the gate bias-stress was studied by comparing the TFT characteristics of the GSZO layer with a tin-doped ZnO (ZTO) layer that lacks gallium. By p...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2016