Effect of 10% Sodium Ascorbate on Bleached Bovine Enamel Surface Morphology and Microhardness

Sodium ascorbate has recently been suggested to compensate decreased bond strength of composite resin to bleached tooth surfaces. The aim of present study was to evaluate the effect of 10% sodium ascorbate on bleached bovine enamel morphology and microhardness considering the possibility of its effect on enamel surface characteristics. A total of 69 bovine enamel slabs were prepared and mounted in acrylic resin. Subsequent to polishing, they were randomly divided into 3 groups of 23 specimens each; 3 for Scanning Electron Microscopy (SEM) analysis and 20 for hardness test. In group 1 the specimens were immersed in distilled water as control group; in group 2 the specimens were bleached with 35% carbamide peroxide for 30 min a week for 3 consecutive weeks; and in group 3 the specimens were exposed to 10% sodium ascorbate for 30 min subsequent to bleaching similar to group 1. After 3 weeks Vickers hardness of the specimens was measured at 3 points with equal distances from each other under a force of 50 g. The mean of the hardness values of each specimen was calculated and data was analyzed by one-way ANOVA (P < 0.05). The highest and lowest microhardness values were observed in group 1 and group 2, respectively. However, there were no statistically significant differences in microhardness between the groups (P = 0.12). The use of 35% carbamide peroxide alone or with 10% sodium ascorbate does not affect bovine enamel hardness. SEM analysis showed a network of sodium ascorbate adsorbed to the bleached enamel surface.