New development of rapid-solidified Fe-Ga sensor/actuator alloy
نویسندگان
چکیده
Rapid-solidification method was applied to make Fe-15at%Ga and Fe-17at%Ga ribbons of 100 μm thickness. These ribbons have large magnetostriction of 270 ppm, where the coercive force exhibits a maximum value. The phenomenon is related to special metallic texture, that is, the ribbon has strongly [001]-oriented textured fine columnar microstructure with grain size of 2~5 μm. The ribbon has little-hysteresis loop of magnetostriction and a good ductility (i.e., full bending is possible). Rapid-solidified Fe-Ga alloy has a promising possibility as a new magnetic-induced sensor/actuator material.
منابع مشابه
Magnetomechanical performance of directionally solidified Fe–Ga alloys
Iron-gallium alloys can produce magnetostrictions of 400 ppm and might serve as mechanically robust actuator/sensing materials. However, for polycrystalline Fe–Ga alloys, the magnetostrictive performance decreases with the increasing deviations from the ideal 100 texture. In this paper, three directionally solidified Fe–Ga alloys with gallium contents of 17, 18.4, and 19.5 at. % were characteri...
متن کاملAlloy Development through Rapid Solidification for Soft Magnetic Application
This chapter describes different rapidly solidified processing routes of soft magnetic alloys and their properties and applications in different areas. Section-2 explains the details of process mechanism. The functions of different alloying elements are discussed with the alloy design of soft magnetic alloys in section-3. The structureproperty correlation is described in section-4. Section-5 hi...
متن کاملDevelopment of Film Actuator Operated by Magnetic Field for Micro-Machine
Fe-Pd alloy films, prepared by using a DC magnetron sputtering method, were developed as a high sensitive actuator, which was driven by the magnetic field. Fe-Pd alloy film shows large magnetostriction and high magnetostrictive susceptibility under 1 kOe. To evaluate the moving potential as magneto-driving actuator, the magnetostrictive properties were measured under different tensile loading s...
متن کاملTEM INVESTIGATION OF RAPIDLY SOLIDIFIED NDFEB HARD MAGNETIC MATERIAL
The surface condition and microstructure of near stoichiometric (Fe823Ndll.8B5.9) Nd-Fe-B alloy ribbons and the effect of melt spinning parameters were investigated using optical, scanning and transmission electron microscopes (SEM, TEM). The formation of gas pockets on the roll surface of the ribbons during melt spinning can prevent heat transform and result in local coarse grains. The local t...
متن کاملEffects of partial crystallinity and quenched-in defects on corrosion of a rapidly solidified Ti–Cu alloy
Rapid solidification by planar flow casting has been found to have introduced deficiencies, viz. partial crystallinity, air pockets and compositional difference in the ribbons of rapidly solidified Ti42⋅9Cu57⋅1 alloy. In order to investigate the effects of these deficiencies on the corrosion of rapidly solidified Ti42⋅9Cu57⋅1 alloy ribbons, electrochemical behaviour of alloy ribbons has been in...
متن کامل