The Microstructure Evolution of a Fe3Al Alloy during the LENS Process

نویسندگان

  • Krzysztof Karczewski
  • Tomasz Durejko
  • Tomasz Czujko
چکیده

A Fe₃Al intermetallic alloy has been successfully prepared by the laser-engineered net shaping (LENS) process. The applied process parameters were selected to provide various cooling rates during the solidification of the laser-melted material. The macro- and microstructure and the micro- and macrotexture of Fe₃Al samples were investigated. The influence of the cooling rate on grain morphology and texture is discussed. For the applied cooling rate range of 0.64 × 10⁴ K/s-2.6 × 10⁴ K/s, the structure is characterized by the presence of columnar grains for which the growth is directed upwards from the substrate. The intensity of the microtexture varies with the height of the sample and the cooling rate. The intensity of the texture increases with the decrease in the cooling rate. The samples that were obtained with low and medium cooling rates are characterized by the well-developed <100> and <111> macrotextures. The Fe₃Al alloy that was produced with a high cooling rate did not show a specific texture, which is reflected in the fairly uniform distribution of the normalized density intensity. Only a very weak texture with a <100> type component was observed.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The Microstructural Evolution of the Coexistence of Spinodal Decomposition and Ordering in Fe-23al Alloy during Aging

Article history: Received: 28.11.2012. Received in revised form: 04.01.2013. Accepted: 15.01.2013. The microstructural evolution of the coexistence of spinodal decomposition and ordering is characterized by metallographic microscopy and transmission electron microscopy in aged Fe-23Al (i.e. Fe-23at%Al) alloy. This paper discusses a phase transition mechanism of the microstructure evolution. The...

متن کامل

Finite element simulation of microstructure evolution during friction stir welding of automotive aluminum parts

7000 series Aluminum alloys are widely used in the automotive industries for structural lightweight components due to their exceptional high strength to weight ratio. However, this class of aluminum alloy is difficult to join by conventional fusion welding techniques so Friction stir welding (FSW) widely is used for welding this alloys. The process has been demonstrated to be effective and is c...

متن کامل

EFFECT OF THE INCLINED COOLING PLATE CHARACTERISTICS ON THE THIXOTROPIC MICROSTRUCTURE OF A356.0 ALUMINUM ALLOY

In the present work microstructural evolution of A356 Aluminum alloy using an inclined cooling plate casting process for thixoforming feedstock production is investigated. The resultant microstructure was evaluated and compared with those of the same alloy produced by the conventional casting process, i.e. directly cast in the same mold without using an inclined cooling plate. It was found that...

متن کامل

Effect of Pre-existing Nano Sized Precipitates on Microstructure and Mechanical Property of Al-0.2wt% Sc Highly Deformed by ARB Process

The effect of pre-existing nano sized precipitates on the mechanisms and rate of grain refinement has been investigated during the severe plastic deformation. A binary Al–0.2Sc alloy, containing coherent Al3Sc particles, of 3.62 nm in diameter has been deformed by accumulative roll bonding up to 10 cycles. The resulting deformed structures were quantitatively analyzed using electron backscatter...

متن کامل

Microstructure evolution and mechanical properties of Mo40/C93200 bimetal processed by compound casting process

Compound casting refers to a process that used to produce bimetals. This study investigates the interface of Mo40/C93200 that is produced by compound casting process. In this research, molten bronze is poured around steel core, interaction between liquid and solid creates a diffusion zone and followed by a transition layer which leads to the creation of diffused region between the interfaces of...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 11  شماره 

صفحات  -

تاریخ انتشار 2018