Residual stresses and mechanical properties of Si3N4/SiC multilayered composites with different SiC layers
نویسندگان
چکیده
The effect of residual stresses on the strength, toughness and work of fracture of Si3N4/SiC multilayered composites with different SiC layers has been investigated. It may be an effective way to design and optimize the mechanical properties of Si3N4/SiC multilayered composites by controlling the properties of SiC layers. Si3N4/SiC multilayered composites with different SiC layers were fabricated by aqueous tape casting and pressureless sintering. Residual stresses were calculated by using ANSYS simulation, the maximum values of tensile and compressive stresses were 553.2 MPa and −552.1 MPa, respectively. Step-like fracture was observed from the fracture surfaces. Fraction of delamination layers increased with the residual stress, which can improve the reliability of the materials. Tensile residual stress was benefit to improving toughness and work of fracture, but the strength of the composites decreased. © 2017 SECV. Published by Elsevier España, S.L.U. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/). Las tensiones residuales y las propiedades mecánicas de compuestos multicapa de Si3N4/SiC con diferentes capas de SiC
منابع مشابه
Thermal Expansion Behavior of Hot-Pressed Engineered Matrices
Advanced engineered matrix composites (EMCs) require that the coefficient of thermal expansion (CTE) of the engineered matrix (EM) matches those of the fiber reinforcements as closely as possible in order to reduce thermal compatibility strains during heating and cooling of the composites. The present paper proposes a general concept for designing suitable matrices for long fiber reinforced com...
متن کاملMicrostructure Characterization and Mechanical Properties of Al-SiCp Composites
In recent years the aluminum matrix composites are gaining wide spread applications in automotive, aerospace, defense, sport and other industries. The reason for this is their exciting properties like high specific strength, stiffness, hardness, wear resistance, dimensional stability and designer flexibility. The present work reports on mechanical properties and microstructure analysis of Al-Si...
متن کاملA STUDY ON SINTERING BEHAVIORS OF COPPER COATED SIC COMPOSITE POWDERS FABRICATED BY ELECTROLESS PLATING AND MECHANICAL PROPERTIES OF THE CONSOLIDATED COMPOSITES
Copper coated SiC powders having three different amounts of copper, in the range of 20-60 wt%, were prepared via electroless coating process. The produced composite powders were uniaxially cold compressed and sintered at different temperatures and times under protective atmosphere. It was found that composite Cu/SiC powders and a relatively dense copper matrix composite with a uniform distribut...
متن کاملResearch on High Performance Fe3Si-Si3N4-SiC Composite Used for Blast Furnace
Excellent Fe3Si-Si3N4-SiC composites were successfully prepared with FeSi75 and SiC as main starting materials by nitridation reaction(at 1300°C for 8Hrs). The material properties were studied; the ferrosilicon nitridation mechanism was analyzed through chemical thermodynamics; phase composition, microstructure, corrosion resistance of products were also investigated. The results are shown that...
متن کامل