Modeling of Yb3+-sensitized Er3+-doped silica waveguide amplifiers
نویسندگان
چکیده
A model for Yb3+ sensitized Er3+-doped silica waveguide amplifiers is described and numerically investigated in the small-signal regime. The amplified spontaneous emission in the ytterbium-band and the quenching process between excited erbium ions are included in the model. For pump wavelengths between 860 and 995 nm, the amplified spontaneous emission in the ytterbium-band is found to reduce both the gain and the optimum length of the amplifier significantly. The achievable gain of the Yb3+-sensitized amplifier is found to be higher than in an Er3+-doped silica waveguide without Yb3+ (18 dB versus 9 dB for a pump power of 100 mW). However, it is important to optimize the Yb-concentration according to the choice of pump wavelength.
منابع مشابه
High-gain polymer optical waveguide amplifiers based on core-shell NaYF4/NaLuF4: Yb3+, Er3+ NPs-PMMA covalent-linking nanocomposites
Waveguide amplifiers have always been significant key components for optical communication. Unfortunately, the low concentration of rare earth ions doped in the host material and the inadequate optimization of the waveguide structure have been the common bottleneck limitations. Here, a novel material, NaYF4/NaLuF4: 20% Yb3+, 2% Er3+ nanoparticle-Polymeric Methyl Methacrylate covalent-linking na...
متن کاملPlanar Er:Yb glass ion exchanged waveguide laser - Electronics Letters
Introduction: Er3+:Yb3+ codoping has become an effective method for producing short, efficient lasers and amplifiers in the long haul telecommunications wavelength range. Ytterbium codoping increases the pump absorption near 980nm and efficient energy transfer between the Yb’’ and the Er3+ ions enables the operation of centimetre long lasers with low Er” concentrations. This mechanism was first...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملNear-field enhancement of infrared intensities for f-f transitions in Er3+ ions close to the surface of silicon nanoparticles.
Erbium doped waveguide amplifiers can be used in optical integrated circuits to compensate for signal losses. Such amplifiers use stimulated emission from the first excited state ((4) I (13/2)) to the ground state ((4) I (15/2)) of Er(3+) at 1.53 µm, the standard wavelength for optical communication. Since the intra-f transitions are parity forbidden for free Er(3+) ions, the absorption and the...
متن کامل