Synthesis and testing of dental ceramic
نویسندگان
چکیده
Zirconia has been recently introduced in prosthetic dentistry for the fabrication of crowns and fixed partial dentures, in combination with CAD/CAM techniques. Zirconia stabilized with Y2O3 has the best properties for these applications. This project aims at producing cast Zirconia blocks primarily for dental application that is more cost effective and biocompatible in comparison to the commercially available zirconia. A simple coprecipitation method was used to produce the zirconia powder; simple, inexpensive and indigenous method of uniaxial compression was employed to cast the zirconia pellet. Further studies have to be carried out to study and improve the densification behaviour, biocompatibility, aesthetics and resistance to masticatory force.
منابع مشابه
Effect of Zirconia Thickness on the Tensile Stress of Zirconia Based All-Ceramic Restorations
Introduction: The purpose of the presented study was to evaluate the effect of zirconia thickness on the tensile stress of zirconia based all-ceramic restorations. Methods: Twenty zirconia disks with 10mm diameter were prepared in two groups using CAD/CAM system. The thickness of zirconia was 0.5mm in first group and 0.3mm in second group. After sintering, 0.4mm glass ceramic porcelain was appl...
متن کاملThe Effect of Lithium Disilicate Ceramic Thickness and Translucency on Shear Bond Strength of Light-cured Resin Cement
Introduction: To achieve acceptable clinical performance, a ceramic veneer must be bonded to enamel by well-polymerized resin cement. Among different factors, thickness and translucency of the ceramic may affect the resin cement polymerization. Thus, the current study evaluated the effect of the thickness and translucency of lithium disilicate ceramic on light-cured resin cement bond strength t...
متن کاملSynthesis of a novel polymeric corrosion inhibitor and investigation of its improvement by the addition of a ceramic powder extracted from corn cob
A new anti-corrosion compound, Melamine Formaldehyde (MF), was formulated by the addition of proper amount of formaldehyde to melamine under specific conditions. This compound was mixed with a novel nano powder, which was extracted from corn cob ash containing SiO2 particles, in order to improve its corrosion inhibition efficiency. This inhibitor provides a high level of protection f...
متن کاملSynthesis of a novel polymeric corrosion inhibitor and investigation of its improvement by the addition of a ceramic powder extracted from corn cob
A new anti-corrosion compound, Melamine Formaldehyde (MF), was formulated by the addition of proper amount of formaldehyde to melamine under specific conditions. This compound was mixed with a novel nano powder, which was extracted from corn cob ash containing SiO2 particles, in order to improve its corrosion inhibition efficiency. This inhibitor provides a high level of protection f...
متن کاملComparison between Biaxial Flexural Strength and Microstructure of Polished and Glaze-Fired Specimens of Zirconia Lithium Silicate Glass Ceramic
Introduction: There has been a growing interest in glass ceramic systems with good esthetics, high fracture resistance, bonding durability, and simplified fabrication techniques using CAD/CAM. The aim of this study was to compare flexural strength in "polished" and "glazed and fired" specimens of zirconium lithium silicate (ZLS) CAD/CAM blocks Celtra Duo. Methods</stron...
متن کاملSilane and bonding of Resins to Ceramic
Silane and bonding of Resins to Ceramic Dr. K. Seyyedan* - Dr. M. Kalalipoor** - Dr. M. Javan***Assistant Professor of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. **Resident of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. Background and Aim: When bonding between two different dental mate...
متن کامل