Mechanism of Abnormal Grain Boundary Ferrite Formation in Hypereutectoid Pearlitic Steels
ثبت نشده
چکیده
منابع مشابه
Dilatometric analysis of cementite dissolution in hypereutectoid steels containing Cr
Cementite dissolution in hypereutectoid steels containing Cr is analyzed using dilatometry combined with the consideration of the carbon content in the austenite. The results suggest that the austenite transformed from the mixture of ferrite and cementite can be approximated to have a carbon content corresponding to equilibrium with ferrite. The overall dissolution behavior of cementite is desc...
متن کاملOptimization of Mechanical Properties of High-Carbon Pearlitic Steels with SI and V Additions
continuous grain-boundary cementite can form and cause THE primary requirements for high-strength wire appliembrittlement.[4,5] Nevertheless, we have found that it is cations are tensile strength, ductility, and formability. Coldpossible to use pearlitic steels with carbon contents greater drawn plain-carbon pearlitic steels have commonly been than 0.8 wt pct without the formation of a continuo...
متن کاملIndian Institute of Technology Kharagpur Comparison of Globularisation Behaviour during Reheating Treatment of Different Pearlitic Microstructures
Pearlitic steels present very interesting mechanical properties when weldability requirements are not too severe. Thin gauge pearlitic steels require at least one intermediate annealing treatment between hot rolling and cold rolling. The globularised cementite in medium carbon steels provides then higher ductility, formability and machinability. On the other hand, in-line induction heating devi...
متن کاملThe Effect of Cooling Rate and Austenite Grain Size on the Austenite to Ferrite Transformation Temperature and Different Ferrite Morphologies in Microalloyed Steels
The effect of different austenite grain size and different cooling rates on the austenite to ferrite transformation temperature and different ferrite morphologies in one Nb-microalloyed (HSLA) steel has been investigated. Three different austenite grain sizes were selected and cooled at two different cooling rates for obtaining austenite to ferrite transformation temperature. Moreover, samples ...
متن کاملGrain Refinement of Dual Phase Steel via Tempering of Cold-Rolled Martensite
A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...