Strength and Interface Analysis

fiber post (GFP) treated or not with phosphoric acid, silane coupling agent, and unfilled resin. GFPs were etched or not with 37% phosphoric acid and different surface coating applied: silane coupling agent, unfilled resin, or both. Composite resin blocks were built around a 4-mm height on the GFP. Unfilled resin (20 s) and composite resin (40 s) were light activated by a light-emitting diode unit. The specimens were stored in distilled water at 37 °C for 24 h. Microtensile bond test was performed using a mechanical testing machine until failure (n=10). The data were analyzed using two-way ANOVA followed by Student-Newman-Keuls’ test (p<0.05). Failure modes were classified as adhesive, mixed, or cohesive failures. Additional specimens (n=3) were made to analyze the bonded interfaces by scanning electron microscopy. The statistical analysis showed the factor ‘surface coating’ was significant (p<0.05), whereas the factor ‘HP etching’ (p=0.131) and interaction between the factors (p=0.171) were not significant. The highest bond strength was found for the silane and unfilled resin group (p<0.05). A predominance of adhesive and cohesive failures was found. Differences regarding the homogeneity and thickness of the unfilled resin layer formed by different GFP surface treatments were observed. The application of silane and unfilled resin can improve the bond strength between GFP and resin composite. Acid Etching and Surface Coating o f G l a s s F i b e r Po s t s : B o n d Strength and Interface Analysis