Solid-State Organization and Ambipolar Field-Effect Transistors of Benzothiadiazole-Cyclopentadithiophene Copolymer with Long Branched Alkyl Side Chains

The solid-state organization of a benzothiadiazole-cyclopentadithiophene copolymer with long, branched decyl-tetradecyl side chains (CDT-BTZ-C14,10) is investigated. The C14,10 substituents are sterically demanding and increase the π-stacking distance to 0.40 nm from 0.37 nm for the same polymer with linear hexadecyls (C16). Despite the bulkiness, the C14,10 side chains tend to crystallize, leading to a small chain-to-chain distance between lamellae stacks and to a crystal-like microstructure in the thin film. Interestingly, field-effect transistors based on solution processed layers of CDT-BTZ-C14,10 show ambipolar behavior in contrast to CDT-BTZ-C16 with linear side chains, for which hole transport was previously observed. Due to the increased π-stacking distance, the mobilities are only 6 × 10 cm2/Vs for electrons and 6 × 10 cm2/Vs for holes, while CDT-BTZ-C16 leads to values up to 5.5 cm2/Vs. The ambipolarity is attributed to a lateral shift between stacked backbones provoked by the bulky C14,10 side chains. This reorganization is supposed to change the transfer integrals between the C16 and C14,10 substituted polymers. This work shows that the electronic behavior in devices of one single OPEN ACCESS Polymers 2013, 5 834 conjugated polymer (in this case CDT-BTZ) can be controlled by the right choice of the substituents to place the backbones in the desired packing.