Leaching Behavior of Al, Co and W from the Al-Alloying Treated WC-Co Tool as a New Recycling Process for WC Hard Scrap
نویسندگان
چکیده
The Al-alloying treated tungsten carbide (WC)-Co tool was subjected to grinding using a jaw crusher and planetary mill followed by three wet chemical treatment steps to establish an effective recycling process for WC scraps, especially those generated as bulky and hard scrap. This alloyed WC tool was readily ground to a powder of 1 mm or less and divided into two portions that were 150 μm in size. The wet chemical treatments enabled us to recover W to 69.44% from the under-sized 150 μm and also obtain WC powders from the over-sized 150 μm with a high purity of 98.9% or more.
منابع مشابه
Effect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملMechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite
In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite p...
متن کاملرفتار سایشی کامپوزیتهای WC-Co و WC-FeAl-B در دمای محیط و 300 درجه سانتیگراد
In this research, the wear behavior of commercial grades of WC-10wt%Co (H10F), WC-40vol%Co and WC-40vol%FeAl-B composites with different amounts of boron from zero to 1000 ppm has been investigated by the pin on disk test method at high temperature. The wear tests were done under load of 40 N, a distance of 100 m and at ambient temperature, 200 ̊C and 300 ̊C. Wear surfaces were examine...
متن کاملInvestigation of the Effect of Homogenization Treatment on Distribution of Alloying Elements, Microstructure and Hardness of Co-Al-W-Ti-Ta-Base Superalloy
The aim of this study was to investigate the effect of temperature and time of homogenization treatment on the microstructure, distribution of alloying elements and hardness of the novel Co-based superalloy Co-7Al-7W-4Ti-2Ta. For this purpose, the specimens were first homogenized at 1250 and 1300 °C for 2, 4, 6 and 8 hours and then water-cooled. Subsequently, the specimens were subjected to har...
متن کاملWear Behavior in Micro and Nano-Structured WC-9Co-0.7VC Cemented Carbide Produced by Rapid Hot Press Sintering
The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...
متن کامل