Electrodeposition of Single Crystalline Co56.48Ni43.52 Alloy Nanowires in AAO Template
نویسندگان
چکیده
Single crystalline cobalt nickel (Co-Ni) alloy nanowires are successfully fabricated using direct current (DC) electrodeposition with in the nanopore of highly ordered anodized aluminum oxide (AAO) template. SEM studies show that the average diameter of the alloy nanowires is approximately equal to 50 nm which corresponds to the pore size of the AAO template. Energy-dispersive X-ray (EDX) analysis confirmed that the Co-Ni alloy nanowires are deposited with 56.48:43.52 atomic ratios. We believe that at high potential the current density of Co nanowires is higher than depositing Ni nanowires which are clear by polarization curves, so content of Co increases in deposited Co56.48Ni43.52 alloy nanowires. Single crystalline Co56.48Ni43.52 alloys can be useful in future to compose and synthesize other metal nanostructures via template-based electrodeposition.
منابع مشابه
Fabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition
Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morph...
متن کاملInvestigations of Microstructures and Magnetic Properties through Off-time between Pulses and Controlled Cu Content in Pulse Electrodeposited NiCu Nanowires
NiCu alloy nanowires arrays were embedded into the anodic aluminum oxide (AAO) template by ac-pulse electrodeposition. Different off-time were used in electrolyte with constant concentration of Ni and Cu and acidity of 3. The effect of deposition parameters on alloy contents was investigated by studying the microstructure and magnetic properties of as-deposited NiCu alloy nanowires. Atomic forc...
متن کاملFabrication of vertically aligned Pd nanowire array in AAO template by electrodeposition using neutral electrolyte
A vertically aligned Pd nanowire array was successfully fabricated on an Au/Ti substrate using an anodic aluminum oxide (AAO) template by a direct voltage electrodeposition method at room temperature using diluted neutral electrolyte. The fabrication of Pd nanowires was controlled by analyzing the current-time transient during electrodeposition using potentiostat. The AAO template and the Pd na...
متن کاملFabrication and characterization of a flow-through nanoporous gold nanowire/AAO composite membrane.
The fabrication of a composite membrane of nanoporous gold nanowires and anodic aluminum oxide (AAO) is demonstrated by the electrodeposition of Au-Ag alloy nanowires into an AAO membrane, followed by selective etching of silver from the alloy nanowires. This composite membrane is advantageous for flow-through type catalytic reactions. The morphology evolution of the nanoporous gold nanowires a...
متن کاملLarge-scale fabrication of single crystalline tin nanowire arrays.
Large-scale single crystalline tin nanowire arrays with preferred lattice orientation along the [100] direction were fabricated in porous anodic aluminium oxide (AAO) membranes by the electrodeposition method using copper nanorod as a second electrode.
متن کامل