Experimental Study on Fatigue Behaviour of Shot-Peened Open-Hole Steel Plates
نویسندگان
چکیده
This paper presents an experimental study on the fatigue behaviour of shot-peened open-hole plates with Q345 steel. The beneficial effects induced by shot peening on the fatigue life improvement are highlighted. The characteristic fatigue crack initiation and propagation modes of open-hole details under fatigue loading are revealed. The surface hardening effect brought by the shot peening is analyzed from the aspects of in-depth micro-hardness and compressive residual stress. The fatigue life results are evaluated and related design suggestions are made as a comparison with codified detail categories. In particular, a fracture mechanics theory-based method is proposed and demonstrated its validity in predicting the fatigue life of studied shot-peened open-hole details.
منابع مشابه
Shot Peening as an Alternative to Fatigue Life Improvement of CK45 Steel Coated with an Electroless Ni-Cu-P
The effect of an electroless Ni-Cu-P coating on the fatigue behavior of quenched and tempered CK45 steel has been investigated. The fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. The results indicate that plating of the base steel leads to a fatigue life reduction. The d...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملEffect of Residual Stresses on Fatigue Strength of Severely Surface Deformed Steels by Shot Peening
The compressive stress distribution below the specimen surface of severely surface deformed steels by shot peening was investigated by using laboratory X-rays and high-energy X-rays from a synchrotron radiation source, SPring-8 in the Japan Synchrotron Radiation Research Institute. Medium carbon steel plates were heat treated in two different conditions. The Vickers hardness of material-A and B...
متن کاملRegression Analysis of Fatigue and Impact Strength of Shot Peened Welded Aisi 304 Austenitic
To upgrade the performance of welded joints the various improvement methods are used. Shot peening is one of the improvement method used to strengthen the properties of welded joints. GMAW process is very well suited for welding of AISI 304 austenitic stainless steels. Regression analysis is the statistical modeling technique, and it is suitable for the majority of predicting problems. It is va...
متن کاملRedesign of Indonesian-made osteosynthesis plates to enhance their mechanical behavior.
Mechanical properties determined by fatigue strength, ductility, and toughness are important measures for osteosynthesis plates in order to tolerate some load-bearing situations caused by muscle contractions and weight-bearing effects. Previous study indicated that Indonesian-made plates showed lower mechanical strength compared to the European AO standard plate. High stress under load-bearing ...
متن کامل