Monomorphic platinum octapod and tripod nanocrystals synthesized by an iron nitrate modified polyol process.
نویسندگان
چکیده
Monomorphic Pt octapod and tripod nanocrystals have been successfully synthesized by an iron nitrate modified polyol process, in which iron nitrate has been proven to be vitally important for slowing down the reduction rate of Pt precursors.
منابع مشابه
Sub-10 nm platinum nanocrystals with size and shape control: catalytic study for ethylene and pyrrole hydrogenation.
Platinum nanocubes and nanopolyhedra with tunable size from 5 to 9 nm were synthesized by controlling the reducing rate of metal precursor ions in a one-pot polyol synthesis. A two-stage process is proposed for the simultaneous control of size and shape. In the first stage, the oxidation state of the metal ion precursors determined the nucleation rate and consequently the number of nuclei. The ...
متن کاملNitrate Removal from Aqueous Solutions Using Granular Activated Carbon Modified with Iron Nanoparticles (RESEARCH NOTE)
Nitrate contamination of water resources and the growing concentration of nitrate endanger human health and the environment and considering its reduction strategies from water resources is important. The aim of this study was to investigate the possibility of removal of nitrate from aqueous solutions using granular activated carbon from grape wood coated with iron nanoparticles. The results sho...
متن کاملSynthesis of Sm–Co and Sm–Co/Fe nanocrystals by reductive annealing of nanoparticles
We report here a simple route for the chemical synthesis of SmCo5 and Sm2Co17 single-phase and SmCo5/Fe composite nanocrystals by polyol reduction of metal precursors and subsequent calcium reductive annealing. Sm2O3 and Co nanoparticles were synthesized first, and nanocrystalline SmCo5 or Sm2Co17, compound with tunable composition was then obtained after the annealing. The composition of the c...
متن کاملIn situ and ex situ studies of platinum nanocrystals: growth and evolution in solution.
In situ studies on the growth and evolution of platinum nanocrystals in solution were carried out using synchrotron-based X-ray diffraction (XRD) techniques. Ex situ low- and high-resolution transmission electron microscopy (TEM) were used to investigate the nanocrystal morphologies through the different growth stages. In a reaction with low precursor concentration, both XRD and TEM results sho...
متن کاملReduction of Sintering during Annealing of FePt Nanoparticles Coated with Iron Oxide
FePt/iron oxide core/shell nanoparticles are synthesized by a two step polyol process with 1,2hexadecanediol as the reducing reagent. Monodispersed 2.6-nm FePt nanoparticles are first obtained by reduction of iron(III) acetylacetonate and platinum(II) acetylacetonate. These preformed FePt nanoparticles are then used as seeds and an iron oxide shell is formed in the second synthesis step. The ro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 47 43 شماره
صفحات -
تاریخ انتشار 2011