Synthesis of nano-sized anatase TiO2 with reactive {001} facets using lamellar protonated titanate as precursor.
نویسندگان
چکیده
Nano-sized anatase TiO(2) with exposed {001} facets was synthesized from lamellar protonated titanate precursor. Owing to small size (ca. 11 nm) and high surface area (155 m(2) g(-1)), the crystals with 26.1% {001} facets exhibited markedly superior photoactivity to reference ca. 76 nm anatase TiO(2) nanosheets with 88.4% {001} facets.
منابع مشابه
Anatase TiO2 Nanoparticles with Exposed {001} Facets for Efficient Dye-Sensitized Solar Cells
Anatase TiO2 nanoparticles with exposed {001} facets were synthesized from Ti powder via a sequential hydrothermal reaction process. At the first-step hydrothermal reaction, H-titanate nanowires were obtained in NaOH solution with Ti powder, and at second-step hydrothermal reaction, anatase TiO2 nanoparticles with exposed {001} facets were formed in NH4F solution. If the second-step hydrotherma...
متن کاملSynthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...
متن کاملSynthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...
متن کاملLow-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets
High-ordered anatase TiO2 nanotube array films coated with exposed high-reactive {001} nanofacets were fabricated by a modified hydrothermal method using amorphous anodic TiO2 nanotube arrays (ATONAs) as starting materials. It was found that the reaction between gas phase HF and solid ATONAs played a key role in the transformation process from amorphous to anatase TiO2, and the TiO2 tubular str...
متن کاملAnatase TiO2 crystals with exposed high-index facets.
Put your best face forward: The performance of TiO2 anatase crystals in energy and environmental applications is normally correlated with the TiO2 crystal facets exposed, and increasing the percentage of highly reactive surfaces is extremely important. A new gas-phase oxidation process using TiCl4 as precursor now yields anatase TiO2 single crystals with primarily high-index {105} facets, which...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 48 55 شماره
صفحات -
تاریخ انتشار 2012