Direct spectrometry: a new alternative for measuring the fluorescence of composite resins and dental tissues.
نویسندگان
چکیده
The aim of this study was to evaluate the fluorescence intensity of different composite resins and compare those values with the fluorescence intensity of dental tissues. Different composite resins were used to make 10 discs (2 mm in depth and 4 mm in diameter) of each brand, divided into groups: 1) Z (Filtek Z350, 3M ESPE), 2) ES (Esthet-X, Dentsply), 3) A (Amelogen Plus, Ultradent), 4) DVS (Durafill-VS, Heraeus Kulzer) with 2 mm composite resin for enamel (A2), 5) OES ([Esthet-X] opaque-OA [1 mm] + enamel-A2 [1 mm]); 6) ODVSI ([Charisma-Opal/Durafill-VSI], opaque-OM (1 mm) + translucent [1mm]), and 7) DVSI ([Durafill- VSI] translucent [2 mm]). Dental tissue specimens were obtained from human anterior teeth cut in a mesiodistal direction to obtain enamel, dentin, and enamel/dentin samples (2 mm). The fluorescence intensity of specimens was directly measured using an optic fiber associated with a spectrometer (Ocean Optics USB 4000) and recorded in graphic form (Origin 8.0 program). Data were submitted to statistical analysis using Dunnet, Tukey, and Kruskall-Wallis tests. Light absorption of the composite resins was obtained in a spectral range from 250 to 450 nm, and that of dental tissues was between 250 and 300 nm. All composite resins were excited at 398 nm and exhibited maximum emissions of around 485 nm. Fluorescence intensity values for all of the resins showed statistically significant differences (measured in arbitrary units [AUs]), with the exception of groups Z and DVS. Group DVSI had the highest fluorescence intensity values (13539 AU), followed by ODVS (10440 AU), DVS (10146 AU), ES (3946 AU), OES (3841 AU), A (3540 AU), and Z (1146 AU). The fluorescence intensity values for the composite resins differed statistically from those of dental tissues (E=1380 AU; D=6262 AU; E/D=3251 AU). The opacity interfered with fluorescence intensity, and group Z demonstrated fluorescence intensity values closest to that of tooth enamel. It is concluded that the fluorescence intensity values were significantly different among the composite resins and compared with dental tissues. The direct spectrofluorimetric method represents a tool for evaluating the fluorescence of composite resins.
منابع مشابه
Staining Beverages and Cigarette Smoke on Composite Resin and Human Tooth Fluorescence by Direct Spectrometry.
INTRODUCTION This study evaluated the fluorescence intensity (FI) of different brands of composite resins (CRs) and compare those values with the FI of human tooth, under the action of cigarette smoke (CI), coffee (CA), and soft drink (CO), measured by direct spectrometry. MATERIALS AND METHODS A total of 30 specimens of each brand (Filtek Z350, Esthet-X, Amelogen, Durafill) were made. Others...
متن کاملEffects of 0.2% Chlorhexidine and Re-polishing on the Color Stability of Nanofilled Composite Resins
Introduction: The growing demand for esthetic dental procedures has resulted in the increased development of new restorative composite resins. The success of composite resin restorations depends on their color stability over time. The present study aimed to evaluate the effects of 0.2% chlorhexidine (CHX) and re-polishing on the color stability of nanofilled composite re...
متن کاملIn vitro Comparative Study of Compressive Strength of Different Types of Composite Resins in Different Periods of Time
To evaluate the ultimate compressive strength of five composite resins after 1 hour, 24 hours, 7 days and 1 month. Twenty four cylindric...
متن کاملBacterial Leakage Assessment for Different Types of Resin-Based Dental Restorations Applied Using Various Placement Methods
Introduction: Although composite resins have improved greatly since their introduction, microleakage is one of the most frequently encountered problems. This study compared the effects of different monomer systems and layering techniques on the bacterial leakage of Cl I composite resin restorations. Methods: Eighty-two sound human third molars were used. The teeth were randomly divided into six...
متن کاملبررسی سازگاری نسجی سه نوع کامپوزیت رزین مورد استفاده در ارتودنسی درمحیط کشت فیبروبلاست های دهانی انسان
Introduction: In orthodontic therapy ,different materials are used and their presence in oral cavity may modify their properties. The purpose of this study was to evaluate the direct and indirect biocompatibility of three orthodontic composite resins on culture of human oral fibroblasts. Methods: This was an interventional experimental study. The biocompatibility of three orthodontic composit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Operative dentistry
دوره 39 4 شماره
صفحات -
تاریخ انتشار 2014