Experimental and numerical investigations of yield surface, texture, and deformation mechanisms in AA5754 over low to high temperatures and strain rates
نویسندگان
چکیده
Department of Mechanical Engineering, University of Maryland, Baltimore County, Baltimore, MD 21250, USA Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6069, USA Department of Materials Science and Metallurgical Engineering, Sunchon National University, Sunchon, Jeonnam 540-742, Republic of Korea NIST Center for Neutron Research, Gaithersburg, MD 20899-8562, USA
منابع مشابه
PREDICTION OF HOT DEFORMATION BEHAVIOUR OF A PH STAINLESS STEEL AT HIGH STRAIN RATES
In this study the hot deformation behaviour of a precipitation hardened (PH) stainless steel at high strain rates has been predicted through hot compression testing. Stress-strain curves were obtained for a range of strain rates from 10-3 to 10+1 S-1 and temperatures from 850 to 1150°C. Results obtained by microstructure and stress-strain curves show that at low temperatures and high strain rat...
متن کاملMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
متن کاملInteraction Between Precipitation and Dynamic Recrystallization in HSLA-100 Microalloyed Steel
Strain induced precipitation in HSLA-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°C to 1100°C and strain rate of 0.001s-1 to 1s-1. The absence of dynamic recrystallization at temperatures below 1000°C was attributedto the influence of dynamic precipitation. The stress relaxation tests showed that strain inducedprecipitation is possible...
متن کاملReview on ultrafined/nanostructured magnesium alloys produced through severe plastic deformation: microstructures
A review on the microstructural evolution in magnesium alloys during severe plastic deformation waspresented. The challenges deserved to achieve ultrafine/ nanostructured magnesium were discussed.The characteristics of the processed materials are influenced by three main factors, including i)difficult processing at low temperatures, ii) high temperature processing and the occurrence ofdynamic r...
متن کاملTexture Evolution in Low Carbon Steel Fabricated by Multi-directional Forging of the Martensite Starting Structuree
It has been clarified that deformation and annealing of martensite starting structure can produce ultrafine-grained structure in low carbon steel. This study aims to investigate the texture evolution and mechanical properties of samples with martensite structure deformed by two different forging processes. The martensitic steel samples were forged by plane strain compression and multi-directio...
متن کامل