Composition Dependence of Structure and Magnetic Properties in Manganese Doped Nanocrystalline ZnO Particles Prepared by Co-Precipitation

نویسندگان

  • Nadia Febiana Djaja
  • Rosari Saleh
چکیده

Mn-doped nanocrystalline ZnO particles have been successfully synthesized at low temperature (80 ̊C) by the coprecipitation method using zinc sulfatehepta hydrate and NaOH. The structural and magnetic properties have been characterized using X-ray diffraction (XRD), Energy dispersive x-ray, vibrating sample magnetometer and electron spin resonance. XRD measurements revealed that the sample posses hexagonal wurzite structure. From the Rietveld refined XRD spectra, the lattice parameters, average crystallite size and microstrain values was obtained. In this range of doping concentrations all samples show an expansion of the lattice parameters relative to the bulk samples. From magnetic measurements we observed the presence of room temperature ferromagnetic order in our Mn-doped ZnO samples.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

An Investigation on Synthesis and Magnetic Properties of Manganese Doped Cobalt Ferrite Silica Core-Shell Nanoparticles for Possible Biological Application

In this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (CoFe2O4)/SiO2 and Manganese doped cobalt ferrite nanoparticles (MnxCo1-xFe2O4 with x= 0.02, 0.04 and 0.06)/SiO2 for possible biomedical application. All the ferrites nanoparticles were prepared by co-precipitation method using FeCl3.6H2O, CoCl2.6H2O and MnCl2.2H2O as precursors, and were silica coated ...

متن کامل

An Investigation on Synthesis and Magnetic Properties of Manganese Doped Cobalt Ferrite Silica Core-Shell Nanoparticles for Possible Biological Application

In this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (CoFe2O4)/SiO2 and Manganese doped cobalt ferrite nanoparticles (MnxCo1-xFe2O4 with x= 0.02, 0.04 and 0.06)/SiO2 for possible biomedical application. All the ferrites nanoparticles were prepared by co-precipitation method using FeCl3.6H2O, CoCl2.6H2O and MnCl2.2H2O as precursors, and were silica coated ...

متن کامل

Room Temperature Ferromagnetism in Cobalt Doped ZnO Nanoparticles

In this work we report synthesis and magnetic characterization of cobalt doped ZnO nanoparticles (with different percent of doped cobalt oxide). Synthesis of the materials was carried out at room temperature by polyacrylamide-gel method, using zink sulfate and cobalt nitrate as source materials, acrylamide as monomer and N,N-methylene bisacrylamide as a lattice reagent. Characterization of the ...

متن کامل

Room Temperature Ferromagnetism in Cobalt Doped ZnO Nanoparticles

In this work we report synthesis and magnetic characterization of cobalt doped ZnO nanoparticles (with different percent of doped cobalt oxide). Synthesis of the materials was carried out at room temperature by polyacrylamide-gel method, using zink sulfate and cobalt nitrate as source materials, acrylamide as monomer and N,N-methylene bisacrylamide as a lattice reagent. Characterization of the ...

متن کامل

Co-precipitation Synthesis of Zinc Oxide (ZnO) Nanoparticles by Zinc Nitrate Precursor

Nanostructured zinc oxide (ZnO) materials have received considerable interest from scientists due to their remarkable performance in electronics, optics and photonics. ZnO nanoparticles were synthesized by co-precipitation method. ZnO nanoparticles were synthesized using Zn(NO3)3 and K2CO3 precursors. The structure of the obtained product was confirmed by the powder X-ray diffraction (XRD) anal...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013