Synthesis and solution rheology of poly[(stearyl methacrylate)-stat-([2-(methacryloyloxy)ethyl] trimethyl ammonium iodide)].
نویسندگان
چکیده
Poly([stearyl methacrylate]-stat-[2-(dimethylamino) ethyl methacrylate]) was synthesised through radical polymerisation using 1,1-diphenyl ethylene (DPE) as a molecular weight controlling agent. The amino groups were further quaternised into a cationic form in order to increase water solubility. Solubility of the polymers in water and a mixed solvent was studied with rotational rheometry. The resulting poly[(stearyl methacrylate)-stat-([2-(methacryloyloxy)ethyl] trimethyl ammonium iodide)] was soluble in water when the amount of stearyl methacrylate (SMA) in the polymer was less than 17 mol%. At higher SMA content, solubility strongly decreased but could be improved by using an organic co-solvent. Viscosity of the SMA-based statistical co-polymers is strongly dependent on polymer composition but solvent quality also has an influence, and the fluidic character can be either Newtonian or shear-thinning, or a weak gel can be formed. Concentration dependence behaviour deviates from that of typical polyelectrolytes. SMA polymers retain low viscosity up to rather high concentrations, but above a certain limiting concentration, the viscosity rapidly increases. This phenomenon is stronger with a higher amount of hydrophobic side-chain. At high co-polymer concentrations no entanglement formation was observed, and rheological behaviour indicates that SMA segments form aggregates in water solution.
منابع مشابه
Amphiphilic cationic polymethacrylates: synthesis, characterization and interactions with cellulose
Aalto University, P.O. Box 11000, FI-00076 Aalto www.aalto.fi Author Arja-Helena Vesterinen Name of the doctoral dissertation Amphiphilic cationic polymethacrylates: synthesis, characterization and interactions with cellulose Publisher School of Chemical Technology Unit Department of Biotechnology and Chemical Technology Series Aalto University publication series DOCTORAL DISSERTATIONS 79/2011 ...
متن کاملSynthesis, characterisation and Pickering emulsifier performance of poly(stearyl methacrylate)–poly(N-2-(methacryloyloxy)ethyl pyrrolidone) diblock copolymer nano-objects via RAFT dispersion polymerisation in n-dodecane† †Electronic supplementary information (ESI) available: PSMA14–PBzMA95 experimental details, assigned NMR spectra, analysis of PSMA14–PNMEPx diblocks prepared at 20% w/w solids and further Pickering emulsion data. See DOI: 10.1039/c6py00138f Click here for additional data file.
متن کامل
Rapid aqueous photo-polymerization route to polymer and polymer-composite hydrogel 3D inverted colloidal crystal scaffolds.
Successful regeneration of biological tissues in vitro requires the utilization of three-dimensional (3D) scaffolds that provide a near natural microenvironment for progenitor cells to grow, interact, replicate, and differentiate to form target tissues. In this work, a rapid aqueous photo-polymerization route was developed toward the fabrication of a variety of polymer hydrogel 3D inverted coll...
متن کاملSynthesis and electrokinetics of cationic spherical nanoparticles in salt-free non-polar media.
Cationic diblock copolymer nanoparticles have been prepared in n-dodecane via polymerization-induced self-assembly (PISA). A previously reported poly(stearyl methacrylate)-poly(benzyl methacrylate) (PSMA-PBzMA) PISA formulation (Chem. Sci. 2016, 7, 5078-5090) was modified by statistically copolymerizing an oil-soluble cationic methacrylic monomer, (2-(methacryloyloxy)ethyl)trimethylammonium tet...
متن کاملKinetic Study of Graft Polymerization of Acrylic Acid and Ethyl Methacrylate onto Starch by Ceric Ammonium Nitrate
Graft polymerization of acrylic acid (AA) and ethyl methacrylate (EMA) onto starch (St) were carried out in aqueous solution using ceric ammonium nitrate (CAN) as redox system under N2 atmosphere. The effect of pH, reaction time, temperature, concentrations of CAN, St, and monomers on the graft yield was investigated. Monomer reactivity was in the following order: AA>EMA.<em...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of colloid and interface science
دوره 351 2 شماره
صفحات -
تاریخ انتشار 2010