Evolution of Voids during Ductile Crack Propagation in an Al Alloy Sheet Toughness Test Studied by Synchrotron Radiation Computed Tomography
نویسندگان
چکیده
The anisotropy of fracture toughness in AA2139 (Al-Cu-Mg) alloy sheet has been investigated via synchrotron radiation computed tomography of arrested cracks in Kahn tear test pieces for different loading cases. The three dimensional distribution and morphology of pores and defects in the as-received state are seen to be anisotropic, with chains of voids and void elongation in the L (longitudinal) direction. For toughness testing in L-T orientation (T is long transverse), voids ahead of the crack grow and link in the L direction. In T-L tests, voids ahead of the crack tip also grow in the loading direction, although a high degree of alignment is retained in the L direction. The present work provides quantitative microstructural data that can be used as input for and validation of recent idealised model formulations, and it is shown that the measured void dimensions and evolution are consistent with measured toughness anisotropy.
منابع مشابه
Quench sensitivity of toughness in an Al alloy: direct observation and analysis of failure initiation at the precipitate free zone
Analysis of toughness in 6156 Al-Mg-Si-Cu sheet has been performed using enhanced Kahn tear tests on samples quenched at different rates. Crack initiation energies were hardly affected by changing water quench temperature from 20°C to 60°C; however a significant reduction was evident on air cooling. Crack propagation energy was reduced for both 60°C water quenched and air cooled materials. Obse...
متن کاملExperimental and computational analysis of toughness anisotropy in an AA2139 Al-alloy for aerospace applications
Fracture toughness anisotropy of AA2139 (Al-Cu-Mg) in T351 and T8 conditions has been investigated via mechanical testing of smooth and notched specimens of different geometries, loaded in the rolling direction (L) or in the transverse direction (T). Fracture mechanisms were investigated via SEM and synchrotron radiation computed tomography (SRCT). Contributions to failure anisotropy are identi...
متن کاملStudy of the flat to slant crack transition in ductile thin sheet material: Simulations and experiments
1 Mines ParisTech, Centre des matériaux, CNRS UMR 7633, BP87 91003 Evry Cedex, France [email protected] Flat to slant crack transition can typically be observed in ductile thin sheet materials. The crack initiates perpendicularly to the loading direction from the notch and then turns to 45° with respect to the loading direction during crack propagation. This phenomenon is, how...
متن کاملExperimental Study of Sable Crack Growth in Thin Aluminium Sheet
Recent failure information from research teams in NASA Langley and others has shown that CTOA based fracture models calibrated on large C(T) and M(T) specimens can be transferred successfully to cracked aircraft fuselage structures for the assessment of their residual strength. A major difficulty that could limit the more extensive use of this failure parameter is its experimental measurement e...
متن کاملTensile Deformation and Fracture Mechanism of Bulk Bimodal Ultrafine-Grained Al-Mg Alloy
The tensile fractures of ultrafine-grained (UFG) Al-Mg alloy with a bimodal grain size were investigated at the microand macroscale using transmission electron microscopy (TEM), scanning electron microscopy (SEM) equipped with focused ion beam (FIB), and optical microscopy. The nanoscale voids and crack behaviors near the tensile fracture surfaces were revealed in various scale ranges and provi...