Failure Test and Finite Element Simulation of a Large Wind Turbine Composite Blade under Static Loading

نویسندگان

  • Xiao Chen
  • Wei Zhao
  • Xiao Lu Zhao
  • Jian Zhong Xu
چکیده

This study presented a failure analysis of a 52.3 m composite wind turbine blade under static loading. Complex failure characteristics exhibited at the transition region of the blade were thoroughly examined and typical failure modes were indentified. In order to predict multiple failure modes observed in the tests and gain more insights into the failure mechanisms of the blade, a Finite Element (FE) simulation was performed using a global-local modeling approach and Progressive Failure Analysis (PFA) techniques which took into account material failure and property degradation. Failure process and failure characteristics of the transition region were satisfactorily reproduced in the simulation, and it was found that accumulated delamination in spar cap and shear web failure at the transition region were the main reasons for the blade to collapse. Local buckling played an important role in the failure process by increasing local out-of-plane deformation, while the Brazier effect was found not to be responsible for the blade failure.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Experimental Investigation and Analysis of Manufacturing Wind Turbine Blades Produced by Hydroforming of Aluminum Alloy AA5754

Development of new technologies and combined with creativity and innovation, plays the fundamental role in developing of any community′s value. Thus, in this research the design and production of hydroforming device was introduced. One of the best and most efficient technologies in the world of metal forming is wind turbine blade producing with hydroforming method which seems as an innovative m...

متن کامل

Experimental Investigation and Analysis of Manufacturing Wind Turbine Blades Produced by Hydroforming of Aluminum Alloy AA5754

Development of new technologies and combined with creativity and innovation, plays the fundamental role in developing of any community′s value. Thus, in this research the design and production of hydroforming device was introduced. One of the best and most efficient technologies in the world of metal forming is wind turbine blade producing with hydroforming method which seems as an innovative m...

متن کامل

Delamination Analysis in Composite Root of a Carbon-Layer Reinforced Wind Turbine Blade

The inconsistencies accompanied with material properties tipically cause the rise of delamination risk in composites made of different types of glass and crabon fibers. In this study, the delamination of a composite beam reinforced with a carbon layer under bending load is investigated. To this end, a small piece of a wind turbine blade root in the form of a heterogeneous laminated plate is sim...

متن کامل

Micro - Structure Characterization of Composite Wind Turbine Blade Following Structural Testing

This paper presents the results of research of the microstructure of the composite blade W55RBVS for the wind turbine of up to 6kW power after structural testing up to failure. The first part of the testing consists of the static testing of the structure up to the moment of the blade failure. The aim of the first part of the test was to define rigidity of the blade W55RBVS, to determine the max...

متن کامل

A semi-analytical model for velocity profile at wind turbine wake using blade element momentum

The shape of wake behind a wind turbine is normally assumed to have a hat shape for the models used in wind farm layout optimization purposes; however, it is know from experimental tests and numerical simulations that this is not a real assumption. In reality, the results of actual measurements and detailed numerical simulation show that the velocity in wake region has a S-shape profile. Th...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2014