Mechanically assisted crevice corrosion of the head-neck taper in a large head metal-on-metal total hip arthroplasty
نویسندگان
چکیده
Taper corrosion of the head-neck junction is a potentially significant and devastating problem facing orthopedic surgeons. We present a case of a 53 year old male who presented for routine follow up for a left, large head, metal on metal total hip arthroplasty five years out. The patient was asymptomatic at the visit. X-rays at the time demonstrated a large amount of medial calcar osteolysis. Serum ion levels revealed a mildly increased cobalt and normal chromium level and hip aspiration revealed brownish fluid. At the time of revision surgery, corrosion of the head-neck taper was found with a normal appearing bearing surface leading to the diagnosis of mechanically assisted crevice corrosion of the head-neck taper with medial calcar osteolysis.
منابع مشابه
Corrosion at the head-neck interface of current designs of modular femoral components: essential questions and answers relating to corrosion in modular head-neck junctions.
There is increasing global awareness of adverse reactions to metal debris and elevated serum metal ion concentrations following the use of second generation metal-on-metal total hip arthroplasties. The high incidence of these complications can be largely attributed to corrosion at the head-neck interface. Severe corrosion of the taper is identified most commonly in association with larger diame...
متن کاملTaper Failure After Large-Diameter Metal-on-Metal Total Hip Arthroplasty.
The use of metal-on-metal bearing surfaces for total hip arthroplasty increased dramatically in the past decade for a variety of reasons, including the advantage of using larger-diameter femoral heads to reduce instability. However, recent research suggesting negative outcomes and high failure rates associated with some of these implants has decreased their use. Further, the use of larger-diame...
متن کاملEvaluation and treatment of painful total hip arthroplasties with modular metal taper junctions.
Modern primary total hip arthroplasty femoral components have evolved to include modular necks. Subsequently, the additional taper junction provides another interface as a potential source for mechanically assisted crevice corrosion, which is a complex process involving fretting and crevice corrosion. Furthermore, it is becoming evident that an adverse local tissue reaction may result in some p...
متن کاملEffect of impact assembly on the interface deformation and fretting corrosion of modular hip tapers: An in vitro study.
Wear and corrosion at the modular head-neck junction has been recognised to be a potential clinical concern, with multiple reports on adverse local tissue reactions and subsequent early failure of metal-on-metal hip replacements. Furthermore, reports on head-neck taper corrosion are also being described with conventional metal-on-polyethylene bearings. Manufacturing tolerances, surgical techniq...
متن کاملCustom titanium sleeve for surgical treatment of mechanically assisted crevice corrosion in the well-fixed, noncontemporary stem in total hip arthroplasty
Adverse local tissue reaction associated with total hip replacement may occur when mechanically assisted crevice corrosion occurs at metal-metal modular junctions in which at least one of the components is fabricated from cobalt-chromium alloy. Complete removal of components may be associated with significant morbidity; when components are well fixed and in acceptable position, it may be approp...