Copper Tube Pitting in Santa Fe Municipal Water Caused by Microbial Induced Corrosion
نویسندگان
چکیده
Many copper water lines for municipal drinking water in Santa Fe, New Mexico USA, have developed pinhole leaks. The pitting matches the description of Type I pitting of copper, which has historically been attributed to water chemistry and to contaminants on the copper tubing surface. However, more recent studies attribute copper pitting to microbial induced corrosion (MIC). In order to test for microbes, the copper tubing was fixed in hexamethyldisilazane (HMDS), then the tops of the corrosion mounds were broken open, and the interior of the corrosion pits were examined with scanning electron microscopy (SEM). The analysis found that microbes resembling actinobacteria were deep inside the pits and wedged between the crystallographic planes of the corroded copper grains. The presence of actinobacteria confirms the possibility that the cause of this pitting corrosion was MIC. This observation provides better understanding and new methods for preventing the pitting of copper tubing in municipal water.
منابع مشابه
Effect of Deformation-Induced Defects on the Microstructure and Pitting Corrosion Behavior of Al-Ag Alloy
In this study, a wide range of combined ageing treatments and cold work deformations in the Al 4.2 wt% Ag alloy matrix were proposed, aiming to investigate the effect of defects such as precipitates (Ag2Al plates) and dislocations on the mechanical and electrochemical behavior of Al–4.2 wt% Ag alloys. Further reductions of thickness from 10 to 60%, decreases the mean size of Ag2...
متن کاملInteractions Between Copper and Chlorine Disinfectants: Chlorine Decay, Chloramine Decay and Copper Pitting
Interactions between copper and chlorine disinfectants were examined from the perspective of disinfectant decay and copper pitting corrosion. Sparingly soluble cupric hydroxide catalyzed the rapid decay of free chlorine, which in turn, led to production of less soluble and more crystalline phases of cupric hydroxide. The catalytic activity of the cupric hydroxide was retained over multiple cycl...
متن کاملInfluence of the Alloying Elements on Uniform and Pitting Corrosion Events Induced by SCN- Anions on Al-6061 and Al-Cu Alloys Surfaces
The electrochemical and corrosion behaviour of Al-6061, Al-4.5%Cu and Al-7.5%Cu alloys were studied in 0.50 M KSCN solution at 25 C. Open-circuit potential, Tafel polarization and ICP-AES measurements were used to study the uniform corrosion process on the surfaces of the tested alloys. Cyclic polarization measurements were employed for pitting corrosion studies. Obtained results were compared ...
متن کاملTheoretical Modeling of the Possibility of Acid Producing Bacteria Causing Fast Pitting Biocorrosion
Biocorrosion, also known as microbiologically influenced corrosion (MIC), is caused by various corrosive biofilms. So far, laboratory experimental MIC pitting tests in the published literature have overwhelmingly focused on sulfate reducing bacteria (SRB) that use sulfate as the terminal electron acceptor because SRB and sulfate are often found at anaerobic pitting sites. Many laboratory pure-c...
متن کاملCopper Pitting and Brass Dezincification: Chemical and Physical Effects
OBJECTIVES: The key hypothesis of this project was that both chemical and physical factors associated with real plumbing systems may influence copper pitting and brass dezincification corrosion, and thus the project was aimed at better understanding these factors. In addition to a comprehensive review of the literature on brass dezincification in potable water systems, experimental work was und...
متن کامل