An investigation into UV light exposure as an experimental model for artificial aging on tensile strength and force delivery of elastomeric chain.

This study investigated the effect of ultraviolet type A light (UVA) exposure on the tensile properties of elastomeric chain. UVA light exposure was used as model for artificial aging, simulating prolonged storage of elastomeric chain. Tensile strength (n = 60) was measured after exposing Ormco, Forestadent and 3M chains to UVA light for 0, 2, 3, and 4 weeks. Force decay was measured (n = 60) using chain exposed for 5, 10, and 14 days. The chains were subsequently stretched at a constant distance and the resulting forces measured at 0, 1, 24 hours and 7, 14, 21, and 28 days. This test simulated a clinical scenario of pre-stretching and subsequent shortening of elastomeric chain. Tensile strength had statistically significant difference and was directly related to the duration of ultraviolet (UV) light exposure. Forestadent chain, which had the second highest value for the 'as received' product, showed the most consistent values over time with the lowest degradation. Ormco showed the lowest values for 'as received' as well as after UV exposure; 3M chain had the highest loss of tensile strength. Force decay was also significantly different. UV light exposure of 10 days or more appears to mark a 'watershed' between products: 3M had most survivors, Forestadent chain had some survivors, depending on the time the chain was stretched for. None of the Ormco product survived UV light exposure for more than 5 days. UVA light exposure may be used as a model for artificial aging as it reduces force delivery and tensile strength of exposed chains.