Optical characterization of Er3þand Yb3þ co-doped barium fluorotellurite glass
نویسندگان
چکیده
Spectroscopic studies of Er3þ/Yb3þ co-doped (Ba,La)-fluorotellurite glass composition have been carried out using standard experimental and theoretical methods. Quantitative analyses of the room temperature absorption and emission spectra as well as the emission lifetimes yield various important spectroscopic parameters such as the radiative decay rates, fluorescence branching ratios, and emission/absorption cross sections. In addition, internal radiative quantum yields have been determined for the infrared emission at 1571 nm and for the upconversion emission at 547 nm. The influence of various non-radiative properties such as multiphonon relaxation, concentration quenching, and quenching by hydroxyl radicals have also been quantitatively estimated and correlated with the observed spectral properties. The comparative studies with the other composition of tellurite and different glasses showed that present glass composition could be a potential candidate for the broadband amplifier. & 2012 Elsevier B.V. All rights reserved.
منابع مشابه
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملPreparation and characterization of nanostructured S and Fe co-doped TiO2 thin film by ultrasonic-assisted spray pyrolysis method
Nanostructured TiO2 and S and Fe co-doped TiO2 thin films with high transparency were prepared on glass substrate through ultrasonic-assisted spray pyrolysis technique. The effects of doping on morphological, optical an...
متن کاملHigh upconversion quantum yield at low pump threshold in Er3þ/Yb3þ doped La2O2S phosphor
In this letter, we report the absolute upconversion quantum yields (QY) for 9% Yb3þ and 1% Er3þ codoped La2O2S and its comparison with NaYF4 doped with 20% Yb 3þ , 2% Er3þ for all the upconversion emissions centered at 410, 550, 667, and 822 nm at various excitation power densities at 977 nm excitation. The maximum upconversion QY for 9% Yb3þ and 1% Er3þ co-doped La2O2S was measured to be 5.837...
متن کاملOrigin of near to middle infrared luminescence and energy transfer process of Er3+/Yb3+co-doped fluorotellurite glasses under different excitations
We report the near to middle infrared luminescence and energy transfer process of Er(3+)/Yb(3+) co-doped fluorotellurite glasses under 980, 1550 and 800 nm excitations, respectively. Using a 980 nm laser diode pump, enhanced 1.5 and 2.7 μm emissions from Er(3+):I13/2→(4)I15/2 and I11/2→(4)I13/2 transitions are observed, in which Yb(3+) ions can increase pumping efficiency and be used as energy ...
متن کامل