Generation of Scratches and Their Effects on Laser Damage Performance of Silica Glass
نویسندگان
چکیده
Scratches are deleterious to precision optics because they can obscure and modulate incident laser light, which will increase the probability of damage to optical components. We here imitated the generation of brittle and ductile scratches during polishing process and endeavored to find out the possible influence of scratches on laser induced damage. Brittle scratches can be induced by spiking large sized abrasives and small abrasives may only generate ductile scratches. Both surface roughness and transmittivity are degraded due to the appearance of brittle scratches while ductile scratches make little difference to surface roughness and transmittance. However, ductile and brittle scratches greatly increase the density of damage about one order of magnitude relative to unscratched surface. In particular, ductile scratches also play an unignorable role in laser induced damage, which is different from previous knowledge. Furthermore, ZrO2 and Al2O3 polished surfaces appear to perform best in terms of damage density.
منابع مشابه
Removal of scratches on fused silica optics by using a CO₂laser.
We investigate the efficiency of local CO₂laser processing of scratches on silica optics in order to enhance the nanosecond UV-laser damage resistance. The surface deformations induced by the process have been measured for different CO₂laser parameters and then the pulse duration and the beam diameter have been chosen accordingly to limit those deformations below 1 µm. From the study of the las...
متن کاملAdvanced Mitigation Process (AMP) for Improving Laser Damage Threshold of Fused Silica Optics
The laser damage precursors in subsurface of fused silica (e.g. photosensitive impurities, scratches and redeposited silica compounds) were mitigated by mineral acid leaching and HF etching with multi-frequency ultrasonic agitation, respectively. The comparison of scratches morphology after static etching and high-frequency ultrasonic agitation etching was devoted in our case. And comparison of...
متن کاملEco-Friendly Hybrid Concrete using Pozzolanic Binder and Glass Fibers
Hybrid Concrete focused on the development of buildings, highways, and other structures of civil engineering. In the current study, various mix combinations have been prepared and tested with different percentages of super-plasticizer at different levels of water reduction for obtaining the optimum mix. Further, study on different properties of hybrid concrete and replacement of ordinary portla...
متن کاملImpact of substrate surface scratches on the laser damage resistance of multilayer coatings
Substrate scratches can limit the laser resistance of multilayer mirror coatings on high-peak-power laser systems. To date, the mechanism by which substrate surface defects affect the performance of coating layers under high power laser irradiation is not well defined. In this study, we combine experimental approaches with theoretical simulations to delineate the correlation between laser damag...
متن کاملInvestigating the Performance Characteristics of Asphaltic Concrete Containing Nano-Silica
Using nano-technology materials in the asphalt pavement industry is new compared with Portland cement concrete. The main objective of this study is to investigate the effects of nano-silica modification on some properties of a penetration grade asphalt cement and a typical asphalt concrete. 60/70 penetration grade bitumen was modified with different percentages of nano-silica (i.e. 1, 3 and 5%,...
متن کامل