Decrease in Hydrogen Embrittlement Susceptibility of 10B21 Screws by Bake Aging
نویسندگان
چکیده
The effects of baking on the mechanical properties and fracture characteristics of low-carbon boron (10B21) steel screws were investigated. Fracture torque tests and hydrogen content analysis were performed on baked screws to evaluate hydrogen embrittlement (HE) susceptibility. The diffusible hydrogen content within 10B21 steel dominated the fracture behavior of the screws. The fracture torque of 10B21 screws baked for a long duration was affected by released hydrogen. Secondary ion mass spectroscopy (SIMS) result showed that hydrogen content decreased with increasing baking duration, and thus the HE susceptibility of 10B21 screws improved. Diffusible hydrogen promoted crack propagation in high-stress region. The HE of 10B21 screws can be prevented by long-duration baking.
منابع مشابه
On the Step Cooling Treatment for the Assessment of Temper Embrittlement Susceptibility of Heavy Forgings in Superclean Steels
When subjected to extended exposure to intermediate service temperatures, Cr–Mo steels, Ni–Cr steels, and 5% Ni steels can become embrittled, with an associated decrease in fracture toughness and a shift in the ductile-to-brittle transition temperature to higher temperatures. Two methods for the investigation of temper embrittlement phenomena are isothermal aging or the use of a step cooling ag...
متن کاملGrain-boundary engineering markedly reduces susceptibility to intergranular hydrogen embrittlement in metallic materials
The feasibility of using ‘‘grain-boundary engineering” techniques to reduce the susceptibility of a metallic material to intergranular embrittlement in the presence of hydrogen is examined. Using thermomechanical processing, the fraction of ‘‘special” grain boundaries was increased from 46% to 75% (by length) in commercially pure nickel samples. In the presence of hydrogen concentrations betwee...
متن کاملA Fracture Analysis of Ti-10Mo-8V-1Fe-3.5Al Alloy Screws during Assembly
Titanium screws have properties that make them ideal for applications that require both a high strength-to-weight ratio and corrosion resistance, such as fastener applications for aviation and aerospace. The fracture behavior of Ti-10Mo-8V-1Fe-3.5Al (TB3) alloy screws during assembly was explored. Besides visual examination, other experimental techniques used for the investigation are as follow...
متن کاملEffects of tungsten on the hydrogen embrittlement behaviour of microalloyed steels
The effects of tungsten (W) additions (0, 0.1, 0.5 and 1 wt.%) on the hydrogen embrittlement behaviour of microalloyed steels were systematically investigated by means of slow strain rate tests on circumferentially notched cylindrical specimens, and the mechanism of hydrogen-induced embrittlement was discussed. W addition is found to increase the activation energy of hydrogen desorption. Micros...
متن کاملWarm Pre-Strain: Strengthening the Metastable 304L Austenitic Stainless Steel without Compromising Its Hydrogen Embrittlement Resistance
Plastic pre-strains were applied to the metastable 304L austenitic stainless steel at both room temperature (20 °C) and higher temperatures (i.e., 50, 80 and 100 °C), and then the hydrogen embrittlement (HE) susceptibility of the steel was evaluated by cathodically hydrogen-charging and tensile testing. The 20 °C pre-strain greatly strengthened the steel, but simultaneously significantly increa...
متن کامل