Characterization of 14 Karat Gold Alloys
ثبت نشده
چکیده
This paper is a continuation of the project we presented at the 2010 Santa Fe Symposium® in which we defined a characterization system and analysis of data on 18K gold alloys. The research carried out since then has enabled us to connect the physical-mechanical characteristics of each alloy with its chemical composition, thereby identifying the best solution possible to produce a specific item. We have decided to report all data related to the analysis of 14K whiteand coloredgold alloys, including alloys suitable for both investment casting and fabrication. We used the same characterization method presented in our 2010 paper, so it will not be specified once again.
منابع مشابه
Promotion of the Cupellation Method for Accurate Determination of Gold Alloy’s Karat Containing Platinum-Group Metals
The main standard method for gold karat determination is the cupellation method. However, this method is not sufficiently accurate to determine gold karat in the presence of insoluble Platinum–Group Metals (PGMs), such as Ir, Ru, and Rh. In this study, for the first time, a complementary method that can be used coupled with the reference cupellation method is presented for the high...
متن کاملEffect of mold temperature on the microstructure and corrosion properties of a 14-karat gold alloy.
The objective of this research was to investigate the effect of mold temperature on grain interior and grain boundary reactions in a14-karat gold alloy. The alloy (Au-15%Ag-3%Pd-24 mass%Cu) was cast into an investment with different mold temperatures (22, 250,400, and 700°C) and then analyzed using SEM, X-ray diffraction, and potentiodynamic polarization tests. Lower mold temperatures(22 and 25...
متن کاملStructural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملبررسی مقاومت باند پرسلن با آلیاژهای دندانپزشکی و اثر پخت مکرر پرسلن بر آن
In this study, porcelain bond strength to three different alloys of Gold-base, pd-Ag and base-Metal were compared and the effect of repeated porcelain sintering on bond strength was evaluated. The obtained results showed best bond strength of porcelain with Gold-base alloy. Pd-Ag and Base-metal alloys showed less strength respectively. During repeated sintering of porcelain, bond strength has...
متن کاملComparative Cyanide and Thiourea Extraction of Gold Based on Characterization Studies (TECHNICAL NOTE)
This study involved preliminary laboratory test work to identify the relative leaching response to cyanidation and thiourea leaching of an oxidized low grade gold ore based on characterization studies. Huge reserves of gold deposits have been reported from different parts of Iran, especially at Neishaboor area with gold grade of approx 4 ppm. For the mineralogical composition, the nature of the...