Fatigue Failure of Structural Steel – Analysis Using Fracture Mechanics
ثبت نشده
چکیده
Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This paper describes an attempt to verify theory of fatigue in fracture mechanics approach with experimentation to determine the constants of crack growth curve. For this, specimen is prepared from the ship building steel and it is subjected to a pulsating bending load with a known defect. Fatigue crack and its nature is observed in this experiment. Application of fracture mechanics approach in fatigue with a simple practical experiment is conducted and constants of crack growth equation are investigated. Keywords—fatigue, fracture mechanics, fatigue testing machine
منابع مشابه
Prediction of fatigue life of reinforced concrete bridges using Fracture Mechanics
With the occurrence of higher and more frequent axle loads, bridges are more solicited by fatigue loading. Bridge elements like deck slabs are subjected to a high number of stress cycles at relatively small stress magnitudes. The application of Fracture Mechanics as a useful tool for the analysis of fatigue crack growth in steel elements was demonstrated by Paris et al. in the early 1960s. With...
متن کاملAssessing and modelling the uncertainty in fatigue crack growth in structural steels
The prediction of the fatigue life of steel structures can be carried out in a number of different ways. A common method at the design stage is to use the so-called S-N approach using design data from a standard such as BS 7910. However, for existing structures containing defects of a known or postulated size, a fatigue life assessment is generally carried out using fracture mechanics. In keepi...
متن کاملBalance Fatigue Design of Cast Steel Nodes in Tubular Steel Structures
Cast steel nodes are being increasingly popular in steel structure joint application as their advanced mechanical performances and flexible forms. This kind of joints improves the structural antifatigue capability observably and is expected to be widely used in the structures with fatigue loadings. Cast steel node joint consists of two parts: casting itself and the welds between the node and th...
متن کاملReliability-based Optimal Inspection for Fracture-critical Steel Bridge Members
To prevent members in steel bridges from fatigue failure, one usually needs to perform frequent periodic bridge inspections and employ detailed inspection methods. This is especially true for fracture-critical members or details. Carrying out these inspections puts a large burden on a transportation agency’s bridge maintenance budget. A systematic reliability-based method for inspection schedul...
متن کاملFatigue Life Prediction of Rivet Joints
Strength reduction in structures like an aircraft could be resulted as cyclic loads over a period of time and is an important factor for structural life prediction. Service loads are emphasized at the regions of stress concentration, mostly at the connection of components. The initial flaw prompting the service life was expected by using the Equivalent Initial Flaw Size (EIFS) which has been re...
متن کامل