Atomic layer deposition and properties of ZrO2/Fe2O3 thin films
نویسندگان
چکیده
Thin solid films consisting of ZrO2 and Fe2O3 were grown by atomic layer deposition (ALD) at 400 °C. Metastable phases of ZrO2 were stabilized by Fe2O3 doping. The number of alternating ZrO2 and Fe2O3 deposition cycles were varied in order to achieve films with different cation ratios. The influence of annealing on the composition and structure of the thin films was investigated. Additionally, the influence of composition and structure on electrical and magnetic properties was studied. Several samples exhibited a measurable saturation magnetization and most of the samples exhibited a charge polarization. Both phenomena were observed in the sample with a Zr/Fe atomic ratio of 2.0.
منابع مشابه
Band-Gap Tuning Of Electron Beam Evaporated Cds Thin Films
The effect of evaporation rate on structural, morphological and optical properties of electron beam evaporated CdS thin films have been investigated. CdS thin film deposited by electron beam evaporation method in 12nm/min and 60nm/min evaporation rates on glass substrates. X-ray diffraction, scanning electron microscopy, UV-Vis-NIR spectroscopy and Atomic Force Microscopy were used to character...
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کاملInvestigation of the Thermodynamic Properties of Surface Ceria and Ceria–Zirconia Solid Solution Films Prepared by Atomic Layer Deposition on Al2O3
The properties of 20 wt % CeO2 and 21 wt % Ce0.5Zr0.5O2 films, deposited onto a γ-Al2O3 by Atomic Layer Deposition (ALD), were compared to bulk Ce0.5Zr0.5O2 and γ-Al2O3-supported samples on which 20 wt % CeO2 or 21 wt % CeO2–ZrO2 were deposited by impregnation. Following calcination to 1073 K, the ALD-prepared catalysts showed much lower XRD peak intensities, implying that these samples existed...
متن کاملSpontaneous nano-clustering of ZrO2 in atomic layer deposited LayZr1-yOx thin films: Part 1 – Material characterization
During atomic layer deposition (ALD) of uniform LayZr1-yOx thin films, spontaneous segregation of ZrO2 nanocrystals takes place that are embedded in an amorphous La2O3 matrix. This occurs if the Zr content in the LayZr1-yOx film is above 30% i.e. if the pulse ratio between the lanthanum precursor and the zirconium precursor is larger than six. We study this clustering phenomena using High resol...
متن کامل