Investigations of White Etching Crack (WEC) Formation under Rolling Contact Fatigue
نویسنده
چکیده
A premature failure mode in steel rolling element bearings called white structure flaking (WSF) occurs in wind turbine gearbox bearings. WSF can occur in as little as 6-24 months of operation. WSF is associated with microstructural alterations called white etching area (WEA) and white etching cracks (WECs) that form in the ~1 mm zone beneath the contact surface. The tribological drivers for WSF are contested. Suggestions of drivers are hydrogen release and diffusion into bearing steel (sourced from the lubricating oil or water contamination) and transient operating conditions, e.g., load, vibrations and slip (see review paper [1] for details and references). Hydrogen has previously been found to diffuse into steel during RCF tests at concentrations between about 0.14.2 ppm.1 For this reason, to replicate this diffusion of hydrogen into the steel during rolling contact fatigue (RCF), hydrogen charging on test specimens/ bearings has been used in various WSF studies. Hydrogen entering steel during rolling contact has been suggested to occur by two mechanisms: (1.) through surface cracks where water contamination or lubricant enters surface cracks, allowing local release of hydrogen ions by tribochemical reactions at crack tip nascent surfaces. (2.) through wear induced nascent surfaces where hydrogen is generated by decomposition of lubricants through catalytic reactions and tribochemical reactions of water.1 The initiation and propagation mechanisms of WSF are contested. Surface initiation at cracks and subsurface initiation by inclusions or impact events have been suggested.1 This group has applied serial sectioning to map subsurface wear volumes of bearings from service and large scale test rigs2 and test specimens from laboratory,3-5 which has allowed investigation of initiation/propagation mechanisms of WSF and thresholds of WSF formation. Extensive FIB/TEM studies to enhance understanding of butterfly crack and WEA formation mechanisms has also been conducted.6
منابع مشابه
Thermal Desorption Analysis of Hydrogen in Non-hydrogen-Charged Rolling Contact Fatigue- Tested 100Cr6 steel
Hydrogen diffusion during rolling contact fatigue (RCF) is considered a potential root cause or accelerator of white etching cracks (WECs) in wind turbine gearbox bearing steels. Hydrogen entry into the bearing steel during operation is thought to occur either through the contact surface itself, or through cracks that breach the contact surface, in both cases by the decomposition of lubricant t...
متن کاملThermal Desorption Analysis of Hydrogen in Non‐hydrogen‐Charged Rolling Contact Fatigue‐Tested 100Cr6 Steel
Hydrogen diffusion during rolling contact fatigue (RCF) is considered a potential root cause or accelerator of white etching cracks (WECs) in wind turbine gearbox bearing steels. Hydrogen entry into the bearing steel during operation is thought to occur either through the contact surface itself or through cracks that breach the contact surface, in both cases by the decomposition of lubricant th...
متن کاملAnalysis of Surface Crack Growth under Rolling Contact Fatigue
Understanding the fatigue crack growth phenomenon in railheads requires a study of driving forces such as the crack tip opening and sliding displacements, under repeated rolling contact. Finite element simulations, allowing elastic-plastic deformation, and mixed-mode crack growth laws were utilized to demonstrate that the fatigue crack growth rates display a minimum after a finite amount of cra...
متن کاملCrack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملRolling contact fatigue in martensitic 100Cr6: subsurface hardening and crack formation
Rolling contact fatigue tests on 100Cr6 steel were carried out with a ballon-rod tester. Microstructural damage was manifested by gradual hardness changes under the subsurface, and microcracks formed adjacent to inclusions; both being evidence of plastic deformation. The hardness increase appears to be due to the development of residual stress, while the microcracks form as a result of the conc...