Effects of Different Heat Treatment on Microstructure, Mechanical and Conductive Properties of Continuous Rheo-Extruded Al-0.9Si-0.6Mg (wt%) Alloy

Al-0.9Si-0.6Mg (wt%) alloy conductive wires were designed and produced by continuous rheo-extrusion process. The effects of different heat treatment on microstructure, mechanical and conductive properties of the wires were studied. Results show that, after T6 heat treatment, conductive property of the alloy increased while elongation decreased with the higher aging temperature and longer aging time. After T8 and T9 heat treatment, acicular strengthening phase β''-Mg2Si homogeneously precipitated, which effectively improved mechanical and conductive property of the alloy. The tensile strength, elongation and resistivity of T8 heat treated alloy reached 336 MPa, 13.7% and 29.3 nΩm respectively. After T9 heat treatment, the alloy’s tensile strength, elongation and resistivity was 338 MPa, 6.0% and 30.2 nΩ·m respectively.