The connective tissue response to Ti, NiCr and AgPd alloys.
نویسندگان
چکیده
The aim of the study was to compare the connective tissue response of Lewis rats to Ti, NiCr and AgPd alloys. It was found that implants were covered by collagen-rich, well vascularized capsules. Titanium was covered by the thinnest capsule (57 ± 20 μm) and AgPd alloy was covered by the thickest capsule (239 ± 50 μm). The PCNA+ cell prevalence in the capsules was lower for titanium than for AgPd and NiCr. Mast cells formed a gradient to a depth of 1200 μm only for titanium implants. Cells with brown to black silver granules in the cytoplasm were observed close to AgPd implants. The results suggest that titanium implants induce a weaker connective tissue response than implants made from NiCr and AgPd alloys.
منابع مشابه
Fabrication of Porous Segments Using Ti-6Al-4V Chips for Orthopaedic Applications
Different methods have been evaluated for manufacturing the porous Ti6Al4V alloys according to decreasing stress shielding phenomenon and increasing mechanical compatibility between the metallic components and the host tissue. For this purpose, in this work Ti6Al4V alloy chips were pressed under 400 MPa pressure and then samples were categorized and heated into two groups at 1000 and 1150℃ unde...
متن کاملFabrication of Porous Segments Using Ti-6Al-4V Chips for Orthopaedic Applications
Different methods have been evaluated for manufacturing the porous Ti6Al4V alloys according to decreasing stress shielding phenomenon and increasing mechanical compatibility between the metallic components and the host tissue. For this purpose, in this work Ti6Al4V alloy chips were pressed under 400 MPa pressure and then samples were categorized and heated into two groups at 1000 and 1150℃ unde...
متن کاملSurface Characterization and Tribological Behaviour of Ti-Ni-P Intermetallic Coatings on Titanium Alloys
In this research, tribological behavior of Ti-Ni-P intermetallic coatings on titanium substrates have been investigated under dry reciprocating conditions. Hardness profile testing results exhibit that high surface hardness has been attained and static indentation result shows that the intermetallic coating has better adhesion strength than the conventional ceramic coatings. In this respect, th...
متن کاملCell response to a newly developed Ti-10Ta-10Nb alloy and its sputtered nanoscale coating
STATEMENT OF PROBLEM The success of titanium implants is due to osseointegration or the direct contact of the implant surface and bone without a fibrous connective tissue interface. PURPOSE The purpose of this study was to evaluate the osteoblast precursor response to titanium - 10 tantalum - 10 niobium (Ti-Ta-Nb) alloy and its sputtered coating. MATERIAL AND METHODS Ti-Ta-Nb coatings were ...
متن کاملTi-alloys: Potential nano-modifier for Rocket Propellants
Composite solid propellants were prepared with and without nano-alloys (Ti-Co, Ti-Ni, Ti-Zn), where nano-alloys used as catalyst. These nano-alloys are prepared by hydrazine reduction method. Catalytic properties of these nanomaterials were measured on Ammonium perchorate/hydroxyterminatedpolybutadiene propellant by thermogravimetery analysis and differential thermal analysis. Both experimental...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Folia histochemica et cytobiologica
دوره 48 3 شماره
صفحات -
تاریخ انتشار 2010