Comparison of two methods of fatigue testing bone cement.
نویسندگان
چکیده
Two different methods have been used to fatigue test four bone cements. Each method has been used previously, but the results have not been compared. The ISO 527-based method tests a minimum of 10 samples over a single stress range in tension only and uses Weibull analysis to calculate the median number of cycles to failure and the Weibull modulus. The ASTM F2118 test regime uses fewer specimens at various stress levels tested in fully reversed tension-compression, and generates a stress vs. number of cycles to failure (S-N) or Wöhler curve. Data from specimens with pores greater than 1mm across is rejected. The ISO 527-based test while quicker to perform, provides only tensile fatigue data, but the material tested includes pores, thus the cement is closer to cement in clinical application. The ASTM regime uses tension and compression loading and multiple stress levels, thus is closer to physiological loading, but excludes specimens with defects obviously greater than 1mm, so is less representative of cement in vivo. The fatigue lives between the cements were up to a factor 15 different for the single stress level tension only tests, while they were only a factor of 2 different in the fully reversed tension-compression testing. The ISO 527-based results are more sensitive to surface flaws, thus the differences found using ASTM F2118 are more indicative of differences in the fatigue lives. However, ISO 527-based tests are quicker, so are useful for initial screening.
منابع مشابه
Influence of test specimen fabrication method and cross-section configuration on tension-tension fatigue life of PMMA bone cement.
Different cyclic loading modes have been used in in vitro fatigue studies of PMMA bone cement. It is unclear which loading mode is most appropriate from the perspective of the in vivo loading experienced by the cement in a cemented arthroplasty. Also, in different in vitro fatigue studies, different test specimen configurations have been used. The present work considers the influence of test sp...
متن کاملCompressive fatigue properties of a commercially available acrylic bone cement for vertebroplasty.
Acrylic bone cements are widely used for fixation of joint prostheses as well as for vertebral body augmentation procedures of vertebroplasty and balloon kyphoplasty, with the cement zone(s) being subjected to repeated mechanical loading in each of these applications. Although, in vertebroplasty and balloon kyphoplasty, the cement zone is exposed to mainly cyclical compressive load, the compres...
متن کاملBone-cement interface of the glenoid component: stress analysis for varying cement thickness.
BACKGROUND Although shoulder arthroplasty is an accepted treatment for osteoarthritis, loosening of the glenoid component, which mainly occurs at the bone-cement interface, remains a major concern. Presently, the mechanical effect of the cement mantel thickness on the bone-cement interface is still unclear. METHODS Finite element analysis of a prosthetic scapula was used to evaluate the effec...
متن کاملOsteonal effects on elastic modulus and fatigue life in equine bone.
We hypothesized that recently formed, incompletely mineralized, and thus, relatively deformable osteons in the equine third metacarpus enhance in vitro load-controlled fatigue life in two ways. Macroscopically, there is a compliance effect, because reduced tissue elastic modulus diminishes the stress required to reach a given strain. Microscopically, there is a cement line effect, in which new ...
متن کاملA new fibre reinforced bone model to pre-clinical test for cement fatigue in total hip replacement
Introduction: The aseptic loosening of cemented hip prostheses, resulting from a combination of mechanical and biological factors, has emerged as one of the major concerns in total hip replacement. In order to investigate the contributing mechanical factors (e.g. cement fatigue, interface mechanics, surface finish) and the long-term effects, pre-clinical test models that are able to reproduce t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Acta biomaterialia
دوره 6 3 شماره
صفحات -
تاریخ انتشار 2010