Experimental Analysis of River Patterns in Silicon Brittle Fractures
نویسنده
چکیده
During propagation of brittle cracks in silicon single crystal,
منابع مشابه
Analysis of the Effects of Wafer Slicing on the Mechanical Integrity of Silicon Wafers (2010-GIT-4)
This paper investigates the effect of crystallographic orientation on the mode of material removal (ductile vs. brittle) in diamond scribing of single crystal silicon (c-Si) and offers an explanation for the observed effects in terms of the combined role of phase transformation and slip generation. Single-point diamond scribing tests are performed on (111), (001) and (110) crystallographic plan...
متن کاملMaterial-independent crack arrest statistics: Application to indentation experiments
An extensive experimental study of indentation and crack arrest statistics is presented for four different brittle materials (alumina, silicon carbide, silicon nitride, glass). Evidence is given that the crack length statistics is described by a universal (i.e., material independent) distribution. The latter directly derives from results obtained when modeling crack propagation as a depinning p...
متن کاملIdeal Brittle Fracture of Silicon Studied with Molecular Dynamics
Silicon is very brittle and a wafer dropped on the floor easily shatters. A clue to explaining why comes from static cracks. Even at room temperature, static cracks in silicon can have tips that are atomically sharp [1], and there is every reason to believe that crystals can be severed very efficiently by the propagation of such sharp cracks. Relations between crack speed and energy consumption...
متن کاملEvaluation of Flow and Fracture Propensity of Notched Steel Plates by Means of a Photoelastic Model
The object of this investigation was to gain a better understanding of the flow and fracture propensity of steel plates in which the Wells-type notch served as the fracture initiator. This type of notch is of importance in experimental investigations of the brittle fracture phenomenon because it successfully initiates low-stress brittle fractures in the wide-plate specimen in which it is used. ...
متن کاملHigh damage tolerance of electrochemically lithiated silicon
Mechanical degradation and resultant capacity fade in high-capacity electrode materials critically hinder their use in high-performance rechargeable batteries. Despite tremendous efforts devoted to the study of the electro-chemo-mechanical behaviours of high-capacity electrode materials, their fracture properties and mechanisms remain largely unknown. Here we report a nanomechanical study on th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2017