Sol-Gel Derived Hydroxyapatite, Fluorhydroxyapatite and Fluorapatite Coatings for Titanium Implants
نویسندگان
چکیده
منابع مشابه
Deposition of Nano-Crystalline Fluor-hydroxyapatite Coatings on Titanium Substrates via Sol-Gel Method
In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...
متن کاملSurface Modification of Anodized Titanium for Calcium Phosphate Coatings
The anodization of titanium involves the formation of a thin, dense and compact, oxide layer. In this process the rutile structure of the original titanium oxide is converted into an anatase structure. It is this anatase structure and how it influences the bonding properties of the sol gel coating of hydroxyapatite (HAp) was the main aim of this research project. "he titanium samples were anodi...
متن کاملSurface characterization of colloidal-sol gel derived biphasic HA/FA coatings.
Hydroxyapatite (HA) powders are ultrasonically dispersed in the precursor of fluoridated hydroxyapatite (FHA) or fluorapatite (FA) to form a "colloidal sol". HA/FA biphasic coatings are prepared on Ti6Al4V substrate via dip coating, 150 degrees C drying and 600 degrees C firing. The coatings show homogenous distribution of HA particles in the FA matrix. The relative phase proportion can be tail...
متن کاملInitial responses of human osteoblasts to sol-gel modified titanium with hydroxyapatite and titania composition.
Sol-gel thin films of hydroxyapatite (HA) and titania (TiO(2)) have received a great deal of attention in the area of bioactive surface modification of titanium (Ti) implants. Sol-gel coatings were developed on Ti substrates of pure HA and TiO(2) and two composite forms, HA+10% TiO(2) and HA+20% TiO(2), and the biological properties of the coatings were evaluated. All the coating layers exhibit...
متن کاملCharacterization and nanomechanical properties of novel dental implant coatings containing copper decorated-carbon nanotubes.
Fluorapatite-titania coated Ti-based implants are promising for using in dental surgery for restoring teeth. One of the challenges in implantology is to achieve a bioactive coating with appropriate mechanical properties. In this research, simple sol-gel method was developed for synthesis of fluorapatite-titania-carbon nanotube decorated with antibacterial agent. Triethyl phosphate [PO4(C2H5)3],...