Porous, Superelastic NiTi Produced by Powder-Metallurgy
نویسندگان
چکیده
Near-stoichiometric NiTi was foamed in the solid state at elevated temperatures through creep expansion of highpressure argon pores previously entrapped during powder consolidation. A sample with 17% porosity was found to be superelastic up to a compressive stress of 800 MPa.
منابع مشابه
High strength, low stiffness, porous NiTi with superelastic properties.
Near-stoichiometric NiTi with up to 18% closed porosity was produced by expansion at 1200 degrees C of argon-filled pores trapped by powder metallurgy within a NiTi billet. When optimally heat-treated, NiTi with 6-16% porosity exhibits superelasticity, with recoverable compressive strains up to 6% at a maximum compressive stress up to 1700 MPa. The apparent Young's modulus of NiTi with 16% poro...
متن کاملNiobium Wires as Space Holder and Sintering Aid for Porous NiTi
When NiTi powder compacts containing Nb wires are heated above 1 170 8C, each Nb wire reacts with adjacent NiTi powders to form a eutectic liquid which wicks into the space between the remaining NiTi powders. This creates a macropore at the location of the Nb wire while eliminating the microporosity between NiTi powders which is filled with a NiTi/Nb eutectic phase after solidification. This no...
متن کاملShape-memory NiTi–Nb foams
A new powder metallurgy technique for creating porous NiTi is demonstrated, combining liquid phase sintering of prealloyed NiTi powders by Nb additions and pore creation by NaCl space-holders. The resulting foams exhibit well-densified NiTi–Nb walls surrounding interconnected pores created by the space-holder, with controlled fraction, size, and shape. Only small amounts of Nb (3 at.%) are need...
متن کاملAn in situ Study of NiTi Powder Sintering Using Neutron Diffraction
This study investigates phase transformation and mechanical properties of porous NiTi alloys using two different powder compacts (i.e., Ni/Ti and Ni/TiH2) by a conventional press-and-sinter means. The compacted powder mixtures were sintered in vacuum at a final temperature of 1373 K. The phase evolution was performed by in situ neutron diffraction upon sintering and cooling. The predominant pha...
متن کاملPorous NiTi alloy prepared from elemental powder sintering
An elemental powder sintering (EPS) technique has been developed for the synthesis of porous NiTi alloy, in which Ni and Ti powders are used as the reactants and TiH2 powder is added as a pore-forming agent and active agent. Effects of various experimental parameters (sintering temperature, sintering time, and TiH2 content) on the porosity, pore size and pore distribution as well as phase compo...