Carbon xerogels were prepared by the polycondensation of resorcinol and formaldehyde using three different solution pH values and the gels were carbonized at three different temperatures. Results show that it is possible to tailor the pore texture of carbon xerogels by adjusting the pH of the initial solution and the carbonization temperature. Materials with different textural properties were obtained and used as catalysts for NO oxidation at room temperature. The NO conversions obtained with carbon xerogels were quite high, showing that carbon xerogels are efficient catalysts for NO oxidation. A maximum of 98% conversion for NO was obtained at initial concentration of NO of 1000 ppm and 10% of O2. The highest NO conversions were obtained with the samples presenting the highest surface areas. The temperature of reaction has a strong influence on NO oxidation: the conversion of NO decreases with the increase of reaction temperature.
منابع مشابه
Xerogel-sequestered silanated organochalcogenide catalysts for bromination with hydrogen peroxide and sodium bromide.
While H2O2 is a powerful oxidant, decomposing into environmentally benign H2O and O2, a catalyst is often required for reactions with H2O2 to proceed at synthetically useful rates. Organotellurium and organoselenium compounds catalyze the oxidation of halide salts to hypohalous acids using H2O2. When sequestered into xerogel monoliths, the xerogel-chalcogenide combinations have demonstrated inc...
متن کاملInfluence of the Synthesis Method for Pt Catalysts Supported on Highly Mesoporous Carbon Xerogel and Vulcan Carbon Black on the Electro-Oxidation of Methanol
Platinum catalysts supported on carbon xerogel and carbon black (Vulcan) were synthesized with the aim of investigating the influence of the characteristics of the support on the electrochemical performance of the catalysts. Three synthesis methods were compared: an impregnation method with two different reducing agents, sodium borohydride and formic acid, and a microemulsion method, in order t...
متن کاملCharacterization of Sol-Gel Derived CuO@SiO2 Nano Catalysts towards Gas Phase Reactions
One distinct concentration of copper ions was embedded into the silica matrix to xerogel form using copper source Cu(NO3)2∙3H2O. The xerogel samples were prepared with using hydrolysis and condensation reactions of TetraEthyl Ortho-Silicate (TEOS) by the sol-gel method. In this investigation, new molar ratio of H2</su...
متن کاملPalladium nanoparticles supported on carbon black powder as an effective anodic catalyst for application in a direct glucose alkaline fuel cell
Palladium nanoparticles supported on carbon black powder (Vulcan XC-72) nanocomposite (Pd/C) are synthesized as the catalyst for the anodic oxidation of glucose for use in a direct glucose alkaline fuel cell (DGAFC). Characterization of the catalyst is carried out using physical and electrochemical methods. It is observed that Palladium nanoparticles are uniformly dispersed onto the carbon blac...
متن کاملPlatinum Nanoparticles Deposited on Oxygen-Containing Functional Groups at Carbon Vulcane XC-72 as a Cathode Catalyst for Direct Methanol Fuel Cell
Surface oxidized carbon vulcane XC-72 is prepared as catalyst support and platinumnanoparticles are chemically anchored onto the modified surface. The nanoparticles of Pt weresynthesized by reduction of H2PtCl6 with sodium borohydride in a 5.5 M buffer solution ofsodium citrate; the complexation of citrate with metal ions is beneficial to the formation ofnanoparticles. The electro-oxidation of ...
متن کامل