Chitosan-Coated Collagen Membranes Promote Chondrocyte Adhesion, Growth, and Interleukin-6 Secretion

نویسندگان

  • Nabila Mighri
  • Jifu Mao
  • Frej Mighri
  • Abdallah Ajji
  • Mahmoud Rouabhia
چکیده

Designing scaffolds made from natural polymers may be highly attractive for tissue engineering strategies. We sought to produce and characterize chitosan-coated collagen membranes and to assess their efficacy in promoting chondrocyte adhesion, growth, and cytokine secretion. Porous collagen membranes were placed in chitosan solutions then crosslinked with glutaraldehyde vapor. Fourier transform infrared (FTIR) analyses showed elevated absorption at 1655 cm-1 of the carbon-nitrogen (N=C) bonds formed by the reaction between the (NH₂) of the chitosan and the (C=O) of the glutaraldehyde. A significant peak in the amide II region revealed a significant deacetylation of the chitosan. Scanning electron microscopy (SEM) images of the chitosan-coated membranes exhibited surface variations, with pore size ranging from 20 to 50 µm. X-ray photoelectron spectroscopy (XPS) revealed a decreased C-C groups and an increased C-N/C-O groups due to the reaction between the carbon from the collagen and the NH2 from the chitosan. Increased rigidity of these membranes was also observed when comparing the chitosan-coated and uncoated membranes at dried conditions. However, under wet conditions, the chitosan coated collagen membranes showed lower rigidity as compared to dried conditions. Of great interest, the glutaraldehyde-crosslinked chitosan-coated collagen membranes promoted chondrocyte adhesion, growth, and interleukin (IL)-6 secretion. Overall results confirm the feasibility of using designed chitosan-coated collagen membranes in future applications, such as cartilage repair.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Water Absorption of Chitosan, Collagen and Chitosan/Collagen Blend Membranes Exposed to Gamma-ray Irradiation

TThis study investigated the water absorption of chitosan, collagen, and chitosan/collagen blend membranes exposed to gamma-ray irradiation. These membranes were produced via the solvent evaporation method. All membranes then underwent irradiation at 15 or 25 kGy gamma-ray doses, while membranes without irradiation were used as controls. After immersing the membranes in distilled water for up t...

متن کامل

Chitosan-based Hyaluronic Acid Hybrid Polymer Fiber for a Novel Three Dimensionalscaffold in Cartilage Tissue Engineering

[Introduction] In cartilage tissue enginnering, a number of studies have shown the importance of selecting the appropriate biomaterials as scaffolds for chondrocyte attachment, for supporting its proliferation and for its synthesis of extra-cellular matrix (ECM). Although a variety of biomaterials, including naturally occurring and synthetic, have been introduced as potential scaffolds for cart...

متن کامل

Carboxymethyl-chitosan protects rabbit chondrocytes from interleukin-1beta-induced apoptosis.

Chondrocyte apoptosis is important in pathogenesis of osteoarthritis. Chitosan is a non-toxic, biodegradable and biocompatible glycosaminoglycan. In this study, the effects of carboxymethyl-chitosan (CM-chitosan), a soluble derivative of chitosan, on chondrocyte apoptosis were investigated. Primary rabbit chondrocytes were cultured and induced to apoptosis by 10 ng/ml interleukin-1beta (IL-1bet...

متن کامل

Guided bone regeneration with asymmetric collagen-chitosan membranes containing aspirin-loaded chitosan nanoparticles

Introduction Membranes allowing the sustained release of drugs that can achieve cell adhesion are very promising for guided bone regeneration. Previous studies have suggested that aspirin has the potential to promote bone regeneration. The purpose of this study was to prepare a local drug delivery system with aspirin-loaded chitosan nanoparticles (ACS) contained in an asymmetric collagen-chitos...

متن کامل

Comparison of Biocompatibility of Various Membranes with Fibroblasts

  Objective: Different techniques have been suggested for the repair of bone defects at the injured sites. Use of biomembranes, or application of plasma rich in growth factor (PRGF) at the site of proliferation of osteoblasts are among the suggested techniques. The current study aimed to compare the biocompatibility of human periodontal ligament fibroblasts (hPLF) cultured on Hypro-Sorb F, Peri...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 8  شماره 

صفحات  -

تاریخ انتشار 2015