Functional polyester fabric through simultaneous aminolysis and nano ZnO synthesis
نویسندگان
چکیده
Here, in situ synthesis of nano zinc oxide, along with aminolysis of polyester fabric, has simultaneously been carried out by using triethanol amine (TEA) and zinc acetate. The ZnO nano particles (NPs) were formed and stabilized on the fabric surface by amine compound at 130 °C for 1 h. The synthesis of nano ZnO particles on the polyester fabric were confirmed by X-ray diffraction (XRD) patterns and scanning electron microscopy (SEM) images. The mean size of ZnO NP was obtained with SEM about 51.38 nm, however, XRD data indicated the crystalline ZnO NPs with a mean crystal size of 14.68 nm on the fabric surface. Further, self-cleaning performance of the treated fabrics was studied by degradation of methylene blue (MB) in aqueous solution under daylight irradiation. The stability of ZnO NPs on the fabric surface was studied by evaluating the self-cleaning and hydrophilicity properties of the samples after standard washing. Also, the hydrophilicity of the treated polyester fabric was improved due to aminolysis of the fabric and the required time for water droplet to spread on the treated fabric after one week exposure to daylight reduced. Overall, TEA was a suitable reducing agent to prepare homogenous ZnO NPs on the polyester fabric.
منابع مشابه
Functional polyester fabric through simultaneous aminolysis and nano ZnO synthesis
Here, in situ synthesis of nano zinc oxide, along with aminolysis of polyester fabric, has simultaneously been carried out by using triethanol amine (TEA) and zinc acetate. The ZnO nano particles (NPs) were formed and stabilized on the fabric surface by amine compound at 130 °C for 1 h. The synthesis of nano ZnO particles on the polyester fabric were confirmed by X-ray diffraction (XRD) pattern...
متن کاملA Study on ZnO Nanorod Arrays Formed on the Surface of Polyester Fabric
A feasibility study on the possible growth of rod-shaped nano size zinc oxide particles on the surface of polyester fabric was investigated. The nanoparticles were produced using a hydrolysis method, with a zinc compound being utilized as the starter material. Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy/energy dispersive X-ray spectrometry (SEM/EDS) and X-ray d...
متن کاملPreparation of Nano-ZnO and Its Application to the Textile on Antistatic Finishing
Nano-ZnO was prepared by direct precipitation method with zinc chloride and sodium carbonate anhydrous as raw materials, and its particle size and dispersion were characterized by TEM. The effects of concentration and the ratio of reactants and reaction temperature on its dispersion in aqueous solution were analyzed and the best reaction conditions were as follows: reaction temperature 60 , ult...
متن کاملStudy on Structural, Mechanical and Functional Properties of Polyester Silica Nanocomposite Fabric
Polyester silica nanocomposite fabrics were prepared by incorporating different concentrations of silica nano particles to the fabric by pad-dry-cure method. The prepared composite fabrics were analyzed in terms of change in their mechanical, structural as well as their functional properties. The surface morphology showed the uniform distribution of silica nano particles on fabric through SEM, ...
متن کامل