Investigation on size tolerance of pore defect of girth weld pipe
نویسندگان
چکیده
Welding quality control is an important parameter for safe operation of oil and gas pipes, especially for high-strength steel pipes. Size control of welding defect is a bottleneck problem for current pipe construction. As a key part of construction procedure for butt-welding of pipes, pore defects in girth weld is difficult to ignore. A three-dimensional non-linear finite element numerical model is established to study applicability of size control indices based on groove shape and softening phenomenon of material in heat-affected zone of practical pipe girth weld. Taking design criteria of pipe as the basis, basic tensile, extremely tensile and extremely compressive loading conditions are determined for pipe stress analysis, and failure criteria based on flow stress is employed to perform stress analysis for pipe girth weld with pore defect. Results show that pipe girth welding stresses of pores at various radial locations are similar. Whereas, stress for pores of different sharpness varied significantly. Besides, tolerance capability of API 5L X90 grade pipe to pore defect of girth weld is lower than that of API 5L X80 grade pipe, and size control index of 3 mm related to pore defect in current standards is applicable to API 5L X80 and X90 grade girth welded pipes with radially non-sharp pore defects.
منابع مشابه
Experimental Study of the Residual Stresses in Girth Weld of Natural Gas Transmission Pipeline
In order to achieve integrated condition in the girth welding of high pressure natural gas transmission pipelines, the weld zones and its surrounding area should have good mechanical properties. Residual stresses are an important defect especially in the girth welding of the pipeline. In this study, two API X70 steel pipes (with spiral seam weld) of 56 inches outside diameter and 0.780 inch wal...
متن کاملLiterature Review: Theory and Application of In-Line Inspection Technologies for Oil and Gas Pipeline Girth Weld Defection
Girth weld cracking is one of the main failure modes in oil and gas pipelines; girth weld cracking inspection has great economic and social significance for the intrinsic safety of pipelines. This paper introduces the typical girth weld defects of oil and gas pipelines and the common nondestructive testing methods, and systematically generalizes the progress in the studies on technical principl...
متن کاملCorrelation between the Weld Residual Stresses and its Tensile and Impact Strength
In this study, the tensile strength, impact strength, and the hardness of the weld are determined. A criterion is proposed for describing the effect of residual stress on the weld mechanical properties. Dimensionless parameters such as Rya (the average of residual stress over the material yield strength), Rym (the maximum residual stress over the material yield strength), ...
متن کاملExperimental determination of normalizing effect on mechanical and metallurgical properties of HSLA API X65 multi-pass girth weld
High strength low alloy steels are widely used in gas industry, so shield metal arc welding in pipelines to transport natural gas from Iran is of great importance. For experimental investigation of seam weld and integrity of girth weld, destructive and non-destructive tests are required. In this article the effects of normal heat treatment on properties of multi pass welding in different situat...
متن کاملFatigue Studies on Stainless Steel Piping Materials and Components: Indian Ahwr
As a part of component integrity test program at Bhabha Atomic Research Centre, fatigue tests on full scale pipe and pipe welds were conducted in addition to CT and TPB specimens. In this paper the outcome of this program is discussed. Specimen testing was conducted to determine the basic cyclic stress strain curve, LCF and FCGR properties. FCGR tests were conducted on CT and TPB specimens to u...
متن کامل