Thin films with high surface roughness: thickness and dielectric function analysis using spectroscopic ellipsometry
نویسندگان
چکیده
An optical surface roughness model is presented, which allows a reliable determination of the dielectric function of thin films with high surface roughnesses of more than 10 nm peak to valley distance by means of spectroscopic ellipsometry. Starting from histogram evaluation of atomic force microscopy (AFM) topography measurements a specific roughness layer (RL) model was developed for an organic thin film grown in vacuum which is well suited as an example. Theoretical description based on counting statistics allows generalizing the RL model developed to be used for all non-conducting materials. Finally, a direct input of root mean square (RMS) values found by AFM measurements into the proposed model is presented, which is important for complex ellipsometric evaluation models where a reduction of the amount of unknown parameters can be crucial. Exemplarily, the evaluation of a N,N'-dimethoxyethyl-3,4,9,10-perylene-tetracarboxylic-diimide (DiMethoxyethyl-PTCDI) film is presented, which exhibits a very high surface roughness, i.e. showing no homogeneous film at all.
منابع مشابه
بررسی ثابت دی الکتریک لایه نازک SiO2با استفاده از آزمون بیضی سنجی
In this paper, we studied the optical behavior of SiO2 thin films prepared via sol-gel route using spin coating deposition from tetraethylorthosilicate (TEOS) as precursor. Thin films were annealed at different temperatures (400-600oC). Absorption edge and band gap of thin layers were measured using UV-Vis spectrophotometery. Optical refractive index and dielectric constant were measured by ell...
متن کاملDielectric function of amorphous tantalum oxide from the far infrared to the deep ultraviolet spectral region measured by spectroscopic ellipsometry
Amorphous tantalum oxide thin films were deposited by reactive rf magnetron sputtering onto @001# silicon substrates. Growth temperature, oxygen partial pressure, and total gas pressure have been varied to obtain thin films with different densities. The thin films were analyzed by glancing angle-of-incidence x-ray diffraction, atomic force microscopy, and variable angle-of-incidence spectroscop...
متن کاملSurface evolution during crystalline silicon film growth by low-temperature hot-wire chemical vapor deposition on silicon substrates
We investigate the low-temperature growth of crystalline thin silicon films: epitaxial, twinned, and polycrystalline, by hot-wire chemical vapor deposition HWCVD . Using Raman spectroscopy, spectroscopic ellipsometry, and atomic force microscopy, we find the relationship between surface roughness evolution and i the substrate temperature 230–350 °C and ii the hydrogen dilution ratio H2/SiH4=0–4...
متن کاملPhase and microstructure investigations of boron nitride thin films by spectroscopic ellipsometry in the visible and infrared spectral range
Phase and microstructure investigations of boron nitride thin films by spectroscopic ellipsometry in the visible and infrared spectral range" (1997). Faculty Publications from the Department of Electrical and Computer Engineering. 64. Spectroscopic ellipsometry over the spectral range from 700 to 3000 cm Ϫ1 and from 1.5 to 3.5 eV is used to simultaneously determine phase and microstructure of p...
متن کاملon Characterization of metal / dielectric multilayers with in - situ ellipsometry
The project was completed on 31 December 2010. In this project, we did simulations for metal/dielectric multilayer structures, their applications as hyperlens for sub-wavelength imaging with resolution beyond diffraction limit, optimized metal (silver) films and started fabrication and characterization of dielectric films with in-situ ellipsometry monitoring the thickness and optical constants....
متن کامل